Vertical ridge augmentation using a porous composite of uncalcined hydroxyapatite and poly-DL-lactide enriched with types 1 and 3 collagen.

Background: Previous studies have shown that porous composite blocks containing uncalcined hydroxyapatite (u-HA; 70 wt%) with a scaffold of poly-DL-lactide (PDLLA, 30 wt%) are biodegradable, encourage appropriate bone formation, and are suitable for use as a bone substitute in vertical ridge augmentation. The present study aimed to accelerate osteogenesis in vertical ridge formation by adding types 1 and 3 collagen to the u-HA/PDLLA blocks and assessing the effect.

Material And Methods: The bone substitute in the present study comprised porous composite blocks of u-HA (70 wt%) with a PDLLA (27-29 wt%) scaffold and enriched with types 1 and 3 collagen (1.7 ~ 3.4 wt%). The control blocks were composed of u-HA (70 wt%) and PDLLA (30 wt%). The materials were formed into 8-mm diameter, 2-mm high discs and implanted onto the cranial bones of six rabbits. The animals were sacrificed 4 weeks after implantation, and histological and histomorphometrical analyses were performed to quantitatively evaluate newly formed bone.

Results: New bone formation occurred with both block types, showing direct contact with the original bone. Mean ± standard deviation bone formation was significantly greater in the experimental blocks (25.6% ± 4.8%) than in the control blocks (17.0% ± 4.7%).

Conclusions: Histological and histomorphometrical observations indicated that new bone was formed with both block types. The u-HA/PDLLA block with types 1 and 3 collagen is a more promising candidate for vertical ridge augmentation than the u-HA/PDLLA alone block.