Research on Creeping Flashover Characteristics of Nanofluid-Impregnated Pressboard Modified Based on Fe₃O₄ Nanoparticles under Lightning Impulse Voltages.

Creeping flashover of mineral-oil-impregnated pressboard under impulse stress is a common insulating failure in oil-immersed transformers, arousing increasing attention. Recent studies have shown that the breakdown strength of transformer oil under positive lightning impulse voltage can be significantly improved through nanoparticles-based modification, and Fe₃O₄ has shown the best improvement in breakdown strength compared to other nanoparticles that have been used. This paper presents the creeping flashover characteristics of pure oil-impregnated pressboard (OIP) and nanofluid-impregnated pressboard (NIP) based on Fe₃O₄ nanoparticles under positive and negative lightning impulse voltages, respectively. It was found that NIP possessed higher resistance to creeping flashover than OIP. The relative permittivities of oil and oil-impregnated pressboard before and after nanoparticles-based modification were measured, and the results revealed that the addition of nanoparticles led to a better match in relative permittivity between oil and oil-impregnated pressboard, and a more uniform electric field distribution. Furthermore, the shallow trap density in NIP was obviously increased compared to that of OIP through the thermally stimulated depolarization current (TSDC), which promoted the dissipation of surface charges and weakened the distortion of the electric field. Therefore, the creeping flashover characteristics of oil-impregnated pressboard were greatly improved with Fe₃O₄ nanoparticles.