Functional artificial vascular meshes from biodegradable polymers have been widely explored for certain tissue engineered meshes. Still, the foreign body reaction and limitation in endothelialization are challenges for such devices. Here, degradable meshes from phase-segregated multiblock copolymers consisting of poly(ε-caprolactone) (PCL) and polydepsipeptide segments are successfully prepared by electrospinning and electrospraying techniques. The pEGFP-ZNF580 plasmid microparticles (MPs-pZNF580) were loaded into the electrospun meshes to enhance endothelialization. These functional meshes were evaluated and . The adhesion and proliferation of endothelial cells on the meshes were enhanced in loaded mesh groups. Moreover, the hemocompatibility and the tissue response of the meshes were further tested. The complete tests showed that the vascular meshes modified with MPs-pZNF580 possessed satisfactory performance with an average fiber diameter of 550 ± 160 nm, tensile strength of 27 ± 3 MPa, Young's modulus of 1. 9 ± 0.2 MPa, water contact angle of 95° ± 2°, relative cell number of 122% ± 1% after 7 days of culture, and low blood platelet adhesion as well as weak inflammatory reactions compared to control groups.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6432533 | PMC |
| http://dx.doi.org/10.3390/polym8030058 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Self-gripping mesh in laparoscopic inguinal hernia repair: A comparative study about surgical time, post-operative pain and recurrence.
J Minim Access Surg
December 2024
Department of General Surgery, Buenos Aires British Hospital, Buenos Aires, Argentina.
Introduction: In laparoscopic inguinal hernia repair (LIHR), fixation means for meshes (FMMs) are commonly used to reduce hernia recurrence risk. Their use may result in post-operative pain (PP) and may even increase surgical time (ST). Recently, self-gripping meshes (SGMs) have been developed, which leave aside fixation devices; they could potentially reduce PP and even decrease ST.
View Article and Find Full Text PDFImage-to-mesh conversion method for multi-tissue medical image computing simulations.
Eng Comput
December 2024
Center for Real-Time Computing, Department of Computer Science, Old Dominion University, Norfolk, VA, United States of America.
Converting a three-dimensional medical image into a 3D mesh that satisfies both the quality and fidelity constraints of predictive simulations and image-guided surgical procedures remains a critical problem. Presented is an image-to-mesh conversion method called CBC3D. It first discretizes a segmented image by generating an adaptive Body-Centered Cubic (BCC) mesh of high-quality elements.
View Article and Find Full Text PDFDesign and development of Vaginal wall mimicking Poly (ε-caprolactone) based nanofibrous prosthetic mesh for pelvic organ prolapse: Evaluation of biocompatibility and antibacterial ability.
Biomed Mater
December 2024
Department of Chemical Engineering, Indian Institute of Technology - Bombay, Powai, Mumbai 400 076, Mumbai, Maharastra, 400076, INDIA.
Mechanical non-conformance of conventionally used transvaginal non-degradable meshes has led to complications like organ perforation, dyspareunia caused by mesh stiffness, and stress shielding. In this study, we have solved the dire need of mimicking the mechanical properties of vaginal wall by designing and developing a soft and elastic mesh made of polycaprolactone (PCL), citric acid modified polyethylene glycol (PEGC) and zinc oxide (ZnO) prepared through electrospinning and is tested in-vitro and in-vivo. Mesh containing 90:10:0.
View Article and Find Full Text PDFDigital Light Processing (DLP) 3D Printing Fabrication of Hydrophobic Meshes Incorporating Fluorinated and Silicone-Based Acrylates Combined with Surface Engineering: Comparison of Their Oil-Water Separation Efficiency.
ACS Omega
December 2024
Department of Chemistry, University of Warwick, Coventry CV4 7AL, U.K.
Hydrophobic materials have been fabricated by DLP vat photopolymerization of isobornyl acrylate-based resins with chemical modification and/or surface geometry engineering. Fluorinated and polydimethylsiloxane (PDMS)-based acrylic monomers are used for chemical modification and are incorporated into the printed materials. The water wettability was significantly reduced and plateaued with as low as 5% (w/w) of the auxillary hydrophobic monomer.
View Article and Find Full Text PDFGuided Bone Regeneration in the Posterior Mandible Using a Resorbable Metal Magnesium Membrane and Fixation Screws: A Case Report.
Case Rep Dent
December 2024
Department of Prosthodontics, Geriatric Dentistry and Craniomandibular Disorder, Charité-Universitätsmedizin Berlin, Aßmannshauser Straße 4-6 14197, Berlin, Germany.
Due to bone loss, implant placement in the posterior mandible is often impossible without prior augentative procedures. The reconstruction of bone defects with horizontal and vertical components using particulated bone grafts requires the placement of a mechanically stable structure for stabilization of the grafting material. Although titanium-reinforced membranes and titanium meshes have been shown to be effective in this indication, the necessity of their removal, often in a separate surgical procedure, is seen as a disadvantage.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!