Tin-Decorated Reduced Graphene Oxide and NaLiNiMnO as Electrode Materials for Sodium-Ion Batteries.

A tin-decorated reduced graphene oxide, originally developed for lithium-ion batteries, has been investigated as an anode in sodium-ion batteries. The composite has been synthetized through microwave reduction of poly acrylic acid functionalized graphene oxide and a tin oxide organic precursor. The final product morphology reveals a composite in which Sn and SnO₂ nanoparticles are homogenously distributed into the reduced graphene oxide matrix. The XRD confirms the initial simultaneous presence of Sn and SnO₂ particles. SnRGO electrodes, prepared using Super-P carbon as conducting additive and Pattex PL50 as aqueous binder, were investigated in a sodium metal cell. The Sn-RGO showed a high irreversible first cycle capacity: only 52% of the first cycle discharge capacity was recovered in the following charge cycle. After three cycles, a stable SEI layer was developed and the cell began to work reversibly: the practical reversible capability of the material was 170 mA·h·g. Subsequently, a material of formula NaLiNiMnO was synthesized by solid-state chemistry. It was found that the cathode showed a high degree of crystallization with hexagonal P2-structure, space group P6₃/mmc. The material was electrochemically characterized in sodium cell: the discharge-specific capacity increased with cycling, reaching at the end of the fifth cycle a capacity of 82 mA·h·g. After testing as a secondary cathode in a sodium metal cell, NaLiNiMnO was coupled with SnRGO anode to form a sodium-ion cell. The electrochemical characterization allowed confirmation that the battery was able to reversibly cycle sodium ions. The cell's power response was evaluated by discharging the SIB at different rates. At the lower discharge rate, the anode capacity approached the rated value (170 mA·h·g). By increasing the discharge current, the capacity decreased but the decline was not so pronounced: the anode discharged about 80% of the rated capacity at 1 C rate and more than 50% at 5 C rate.