Background/purpose: Intraradicular moisture is not standardized and alters the sealing properties and adhesion of root sealers. The aim of this work was to evaluate the effect of different moisture on the constitution of bioceramic sealers.
Materials And Methods: The sealers were evaluated before mixing, and after setting using X-ray diffraction (XRD), Energy Dispersive Analysis (EDX) and Scanning Electron Microscope (SEM) techniques. Twenty four extracted teeth were prepared and assigned to four groups according to the moisture conditions: (1) dry: using ethanol as final irrigation, (2) normal: using paper points until the last one appeared dry, (3) moist: using a Luer adapter for 5 s followed by 1 paper point, and (4) wet: the canals remained totally flooded. The roots were filled with MTA Fillapex and Endosequence BC and kept in phosphate buffer solution at 37 °C for 10 days. Each root was sectioned transversally and longitudinally. The sealers harvested from longitudinal sections were analysed using XRD. Whilst the transverse sections were analysed using SEM/EDX.
Results: The XRD analysis showed MTA Fillapex composed of Bismuth trioxide, calcium silicate and tricalcium aluminate. The intensity of peaks in the wet condition was reduced. Endosequence BC contained mainly calcium silicate, calcium silicate hydrate, zirconia and calcium hydroxide. The wet condition showed a small increase in hydrated calcium silicate. The EDX analysis showed changes in the elemental concentrations with different moisture conditions. The surface morphology differed with different moisture conditions.
Conclusion: Tested sealers have different constitution that not affected by the degree of moisture. However, it changed their relative quantity.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6395366 | PMC |
| http://dx.doi.org/10.1016/j.jds.2017.03.008 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Influence of elevated temperature exposure on the residual compressive strength and radiation shielding efficiency of ordinary concrete incorporating granodiorite and ceramic powders.
Sci Rep
January 2025
Physics Department, Faculty of Science, Fayoum University, Fayoum, Egypt.
This research investigates the potential of utilizing types of construction waste as partial cement replacements within concrete formulations. Notably, granodiorite and ceramic powders were introduced at varying substitution ratios. The impact of these waste materials on the compressive strength and radiation shielding effectiveness of traditional concrete was evaluated under both ambient and elevated temperature conditions.
View Article and Find Full Text PDFBiomineralization reaction from nanosized calcium silicate: A new method for reducing dentin hypersensitivity.
J Dent Sci
January 2025
Department of Conservative Dentistry, School of Dentistry and Dental Research Institute, Seoul National University, Seoul, Republic of Korea.
Background/purpose: This study assessed the ability of experimental materials consisting of dicalcium silicate (DCS) and tricalcium silicate (TCS) with nanosized particles to form intratubular crystals under phosphate-buffered saline (PBS) and the effect on dentin permeability reduction.
Materials And Methods: By isolating the cervical part of the extracted premolars, 195 specimens were obtained. Two experimental materials (DCS/TCS and TCS) were applied to the dentin surface by brushing and stored in PBS (n = 65).
Antimicrobial properties of bimetallic-containing mesoporous bioglass against .
J Dent Sci
January 2025
Department of Fragrance and Cosmetic Science, College of Pharmacy, Kaohsiung Medical University, Kaohsiung, Taiwan.
Background/purpose: Various pulp-covering materials offer advantages in regenerative root canal treatment, but each has limitations, highlighting the need for more effective antibacterial strategies for pulp repair and regeneration. Mesoporous bioactive glasses (MBG) show significant biological activity, making them valuable in tissue/dental repair. Silver-incorporated MBG exhibits promising antibacterial effects against various bacteria; copper ions are crucial in regulating angiogenesis signals.
View Article and Find Full Text PDFPhysical, chemical and biological properties of MTA Angelus and novel AGM MTA: an in vitro analysis.
BMC Oral Health
January 2025
School of Dentistry, Shahid Beheshti University of Medical Sciences, Tehran, Iran.
Introduction: Mineral trioxide aggregate (MTA) is a calcium silicate-based cement that has changed conventional dental therapeutic approaches. This study aimed to evaluate physical, chemical and biological properties of novel AGM MTA, in comparison with MTA Angelus.
Methods: The samples were prepared according to the manufacturer's instructions.
Green building development utilising modified fired clay bricks and eggshell waste.
Sci Rep
January 2025
PV Unit, Solar and Space Research Department, National Research Institute of Astronomy and Geophysics (NRIAG), Helwan, Cairo, Egypt.
The inadequate thermal insulation of the building envelope contributes significantly to the high power consumption of air conditioners in houses. A crucial factor in raising a building's energy efficiency involves utilizing bricks with high thermal resistance. This issue is accompanied by another critical challenge: recycling and disposing of waste in a way that is both economically and environmentally beneficial, including using it to fuel industrial growth, in order to reduce the harmful effects of waste on the environment as waste generation in our societies grows.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!