Nanostructured Fe,Co-Codoped MoO₃ Thin Films.

Molybdenum oxide (MoO₃) and Fe,Co-codoped MoO₃ thin films obtained by spray pyrolysis have been in-depth investigated to understand the effect of Co and Fe codoping on MoO₃ thin films. The effect of Fe and Co on the structural, morphological and optical properties of MoO₃ thin films have been studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy-dispersive X-ray analysis (EDAX), optical and photoluminescence (PL) spectroscopy, and electropyroelectric methods. The XRD patterns demonstrated the formation of orthorhombic α-MoO₃ by spray pyrolysis. SEM characterization has shown an increase in roughness of MoO₃ thin films by Fe and Co doping. Optical reflectance and transmittance measurements have shown an increase in optical band gap with the increase in Fe and Co contents. Thermal conductivity and thermal diffusivity of Fe,Co-doped MoO₃ were 24.10⁻25.86 WmK and 3.80 × 10⁻5.15 × 10 m²s, respectively. MoO₃ thin films have shown PL emission. Doping MoO₃ with Fe and Co increases emission in the visible range due to an increase number of chemisorbed oxygen atoms. The photodegradation of an aqueous solution of methylene blue (MB) depended on the content of the codoping elements (Fe,Co). The results showed that a degradation efficiency of 90% was observed after 60 min for MoO₃: Fe 2%-Co 1%, while the degradation efficiency was about 35% for the undoped MoO₃ thin film.