Ground coat enamels for low carbon steel that contain silica as a mill addition have been developed to study the changes of their properties. Acid-resistant commercial enamel where silica addition was varied from 0 to 10.0 wt % was used for this investigation. The effects of the addition on the corrosion resistance, thermal properties, electrical properties, and mechanical adherence of the enamel to low carbon steel were studied. The corrosion resistance of the steel enameled coupons was tested using a salt spray (fog) apparatus for time periods reaching 168 h at room temperature. It was found that, although the density was not affected, the adherence decreased with an increase in silica content. As expected, the silica addition decreased the coefficient of thermal expansion, which is directly related to the increasing stress between the glass and steel in accordance with the adherence results. A mill addition of 7.5 wt% of silica to the samples was sufficient to obtain adequate enamel adherence and good corrosion resistance. Furthermore, the addition of silica influenced the electrical conductivity and dielectric permittivity measurements at room temperature and the conductivity measured in a wide frequency range (1 Hz⁻1 MHz). The dielectric permittivity measured at 1 MHz showed decrease after the addition of up to 7.5 wt% of silica.
Download full-text PDF |
Source |
---|---|
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6356640 | PMC |
http://dx.doi.org/10.3390/ma12020248 | DOI Listing |
J Appl Biomater Funct Mater
January 2025
MOE Key Lab for Liquid-Solid Structure Evolution and Materials Processing, Shandong University, Jinan, China.
In current study, microstructural, mechanical and corrosion behaviour were investigated with incorporation of dual reinforced AZ91D surface composites. This research was carried out for enhancement of the bio-degradability in biological environment. The surface composites were successfully fabricated by friction stir processing method with a rotation speed of 800 rpm, travel speed of 80 mm/min and 2.
View Article and Find Full Text PDFSci Rep
January 2025
Physical Chemistry Department, National Research Centre, 33 El Bohouth Street, P.O.12622, Dokki, Giza, Egypt.
Archaeological coins are considered essential sources of historical documentation. Over time, they are subjected to corrosion processes that gradually alter their appearance, shape, and composition. This study aims to evaluate the effects of the patina and/or protective coating on the corrosion process.
View Article and Find Full Text PDFPLoS One
January 2025
School of Mechanical Engineering, Liaoning Technical University, Fuxin, China.
Titanium alloy is known for its low thermal conductivity, small elastic modulus, and propensity for work hardening, posing challenges in predicting surface quality post high-speed milling. Since surface quality significantly influences wear resistance, fatigue strength, and corrosion resistance of parts, optimizing milling parameters becomes crucial for enhancing service performance. This paper proposes a milling parameter optimization method utilizing the snake algorithm with multi-strategy fusion to improve surface quality.
View Article and Find Full Text PDFHeliyon
January 2025
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Hafez Ave., P.O. Box 15875-4413, Tehran, Iran.
This study investigates the impact of MgO nanoparticles (0, 0.1, 0.5, and 1 wt%) on the corrosion behavior of hot-dipped galvalume (Zn-55Al-1.
View Article and Find Full Text PDFSci Rep
January 2025
I-Form Advanced Manufacturing Research Centre, Dublin City University, Dublin, Ireland.
In the realm of materials science and engineering, the pursuit of advanced materials with tailored properties has been a driving goal behind technological progress. Scientific interest in laser powder bed fusion (L-PBF) fabricated NiTi alloy has in recent times seen an upsurge of activity. In this study, we investigate the impact of varying volume energy density (VED) during L-PBF on the microstructure and corrosion behaviour of NiTi alloys in both scan (XY) and built (XZ) planes.
View Article and Find Full Text PDFEnter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!
© LitMetric 2025. All rights reserved.