Electrostatic potential and valence modulation in LaSrMnO thin films.

The Mn valence in thin film LaSrMnO was studied as a function of film thickness in the range of 1-16 unit cells with a combination of non-destructive bulk and surface sensitive X-ray absorption spectroscopy techniques. Using a layer-by-layer valence model, it was found that while the bulk averaged valence hovers around its expected value of 3.3, a significant deviation occurs within several unit cells of the surface and interface. These results were supported by first principles calculations. The surface valence increases to up to Mn, whereas the interface valence reduces down to Mn. The change in valence from the expected bulk value is consistent with charge redistribution due to the polar discontinuity at the film-substrate interface. The comparison with theory employed here illustrates how this layer-by-layer valence evolves with film thickness and allows for a deeper understanding of the microscopic mechanisms at play in this effect. These results offer insight on how the two-dimensional electron gas is created in thin film oxide alloys and how the magnetic ordering is reduced with dimensionality.