Objectives: To evaluate and compare the outcomes of shear (S) and microtensile (μT) bond strength tests of CAD/CAM fiber-reinforced composite (FRC) to dentin. Aging with either fatigue or thermocycling were conducted for comparison with baseline microtensile group.
Methods: CAD/CAM FRC (Trinia, Bicon LLC, Boston, USA) blocks were milled to 3-mm diameter cylinders for shear and to blocks (5×5×5mm) for μT. Sixty extracted human molars were flattened to obtain dentin surfaces and randomly divided in four groups (n=15): (1) SC: samples tested in shear 24h after bonding; (2) μTC: samples tested in μT 24h after bonding); (3) μTF: samples submitted to mechanical fatigue prior to μT test, and; (4) μTT: thermocycling prior to μT test. Bonding system was applied onto the FRC material (Cera-Resin Bond, CRB, Shofu Dental, Kyoto, Japan). A conventional three-step adhesive system (All-bond 3, Bisco, Schaumburg, USA) was use with a self-cure resin cement (C&B resin cement, Bisco, Schaumburg, USA). Bond strength tests were conducted at 0.75mm/min and data analyzed using Weibull distribution (p<0.05).
Results: Weibull contour plots showed a significantly lower characteristic strength (η) and Weibull modulus (m) for SC (η=6.9MPa and m=1.4) compared to μTC (η=20.9MPa and m=4.5). Fatigued and thermocycled μT groups presented significantly reduced characteristic strength (η=3.1MPa and η=4.1MPa, respectively) compared to μTC. Weibull modulus was significantly reduced only for SC and μTF groups compared μTC. Failure predominantly occurred at the cement/FRC interface.
Significance: FRC bonded to dentin samples presented lower Weibull modulus and characteristic bond strength when immediately tested in shear compared to microtensile. Aging through thermocycling or mechanical fatigue significantly reduced the characteristic strength in microtensile testing, with the majority of failures emerging between restoration material and cement interface.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2018.08.302 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Long-Term Dentin Bonding Performance of Universal Adhesives: The Effect of HEMA Content and Bioactive Resin Composite.
J Funct Biomater
December 2024
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo 060-8586, Japan.
This study investigated the effects of resin composites (RCs) containing surface pre-reacted glass ionomer (S-PRG) filler on the dentin microtensile bond strength (μTBS) of HEMA-free and HEMA-containing universal adhesives (UAs). Water sorption (WS) and solubility (SL), degree of conversion (DC), and ion release were measured. The UAs BeautiBond Xtreme (BBX; 0% HEMA), Modified Adhesive-1 (E-BBX1; 5% HEMA), Modified Adhesive-2 (E-BBX2; 10% HEMA), and two 2-step self-etch adhesives (2-SEAs): FL-BOND II (FBII; with S-PRG filler) and silica-containing adhesive (E-FBII) were used.
View Article and Find Full Text PDFEvaluation of the Effect of Chitosan-Based Irrigation Solutions on the Bond Strength of Mineral Trioxide Aggregate to Bulk-Fill Composite.
J Funct Biomater
December 2024
Department of Endodontics, Faculty of Dentistry, Gazi University, 06490 Ankara, Türkiye.
Bond strength between repair and restorative materials is crucial for endodontic success. This study assessed the effects of the following final irrigation solutions on the bond strength of mineral trioxide aggregate (MTA) to a bulk-fill composite: (1) 17% Ethylenediamine tetraacetic acid (EDTA); (2) 2% Chlorhexidine (CHX); (3) 0.2% chitosan; (4) 0.
View Article and Find Full Text PDFEffect of Mechanical Surface Treatment on Shear Bond Strength of Orthodontic Brackets to 3D Printed and Milled CAD/CAM Provisional Materials: An In Vitro Study.
J Funct Biomater
November 2024
King Abdullah International Medical Research Center, Riyadh 11481, Saudi Arabia.
The aim of the study is to assess the impact of mechanical surface treatments on the shear bond strength (SBS) of orthodontic brackets bonded to three-dimensional (3D) printed and milled CAD/CAM provisional materials. Sixty cylindrical samples were fabricated for each provisional material. Samples were treated with one of the following surface treatments: aluminum oxide airborne particle abrasion, diamond bur rotary instrument roughening, and phosphoric acid etching (control).
View Article and Find Full Text PDFComparative Assessment of Push-Out Bond Strength and Dentinal Tubule Penetration of Different Calcium-Silicate-Based Endodontic Sealers.
Dent J (Basel)
December 2024
Faculty of Dentistry, Iuliu Hatieganu University of Medicine and Pharmacy, 400012 Cluj-Napoca, Romania.
Adhesion within endodontic obturation material and root canal walls improves the efficacy of the endodontic treatment by establishing a barrier that inhibits reinfection and entombs residual bacteria. This study evaluates the push-out bond strength (POBS) of calcium silicate sealers compared to an epoxy-resin-based sealer. A total of 36 extracted mono-radicular teeth were prepared with Pro Taper Ultimate and irrigated with 5.
View Article and Find Full Text PDFEvaluation of Shear Bond Strength of Lithium Disilicate Veneers Using Pre-heated Resin Composite With Two Conventional Resin Cements: An In Vitro Study.
Cureus
November 2024
Department of Endodontic and Operative Dentistry, Damascus University, Damascus, SYR.
Objectives This study aimed to compare the shear bond strength of three resin cements (light-cured resin cement, pre-heated composite resin, and dual-cured self-adhesive resin cement) when bonding to lithium disilicate discs. Materials and methods Thirty-six discs made of lithium disilicate were fabricated and etched with 9.5% (HF), and 36 human premolars were collected and immersed in the acrylic molds, then randomly divided into three equal groups (n = 12): Group 1: light-cured resin cement, Group 2: pre-heated resin composite, and Group 3: dual-cured resin cement.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!