A newly designed hydroxyapatite-polyurethane (HA-PU) composite scaffold was prepared by polymerizing glyceride of castor oil (GCO) with isophorone diisocyanate (IPDI) and HA as fillers. The aim of this study was to determine the effect of HA fillers on the mechanical properties and osteogenesis capacity of the composite scaffolds. The physical and biological properties of the scaffold were evaluated by SEM observation, mechanical testing, cell culture and animal experiments. The results showed that HA fillers enhanced the mechanical properties of PU composite scaffolds such as compressive strength and elastic modulus. The mechanical properties of the scaffolds were seen to increase with increase in HA loading. The compressive strength of composite scaffold with 0 wt%, 20 wt%, 40 wt% of HA was 0.6 ± 0.1 MPa, 2.1 ± 0.1 MPa, and 4.6 ± 0.3 MPa, respectively. In vitro biodegradation studies of scaffolds were carried out. The results showed that all of the scaffolds were susceptible to cholesterol esterase (CE) -catalyzed degradation. HA-PU composite scaffolds exhibited a high affinity to osteoblastic cells and were good template for cell growth and proliferation. When implanted in bone defects of rats, PU scaffolds incorporated HA were biocompatible with the tissue host and had no immune rejection. Moreover, the higher the loading of HA in the composite scaffold, the better chances of osteogenesis. It confirmed that the prepared HA-PU composite scaffolds can be promising candidate for bone repair and bone tissue engineering.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.jmbbm.2018.08.028 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Multi-channel learning for integrating structural hierarchies into context-dependent molecular representation.
Nat Commun
January 2025
University of Pittsburgh, Department of Computer Science, Pittsburgh, PA, 15260, USA.
Reliable molecular property prediction is essential for various scientific endeavors and industrial applications, such as drug discovery. However, the data scarcity, combined with the highly non-linear causal relationships between physicochemical and biological properties and conventional molecular featurization schemes, complicates the development of robust molecular machine learning models. Self-supervised learning (SSL) has emerged as a popular solution, utilizing large-scale, unannotated molecular data to learn a foundational representation of chemical space that might be advantageous for downstream tasks.
View Article and Find Full Text PDFAn Overview on Bioactive Glasses for Bone Regeneration and Repair: Preparation, Reinforcement, and Applications.
Tissue Eng Part B Rev
January 2025
Materials Science and Engineering, School of Materials and Chemistry, University of Shanghai for Science & Technology, Shanghai, China.
Synthetic bone transplantation has emerged in recent years as a highly promising strategy to address the major clinical challenge of bone tissue defects. In this field, bioactive glasses (BGs) have been widely recognized as a viable alternative to traditional bone substitutes due to their unique advantages, including favorable biocompatibility, pronounced bioactivity, excellent biodegradability, and superior osseointegration properties. This article begins with a comprehensive overview of the development and success of BGs in bone tissue engineering, and then focuses on their composite reinforcement systems with biodegradable metals, calcium-phosphorus (Ca-P)-based bioceramics, and biodegradable medical polymers, respectively.
View Article and Find Full Text PDFResearch Progress in 3D Printed Biobased and Biodegradable Polyester/Ceramic Composite Materials: Applications and Challenges in Bone Tissue Engineering.
ACS Appl Mater Interfaces
January 2025
Laboratory of Biomass and Green Technologies, Gembloux Agro-Bio Tech, University of Liège, Passage des Déportés, 2, 5030 Gembloux, Belgium.
Transplantation of bone implants is currently recognized as one of the most effective means of treating bone defects. Biobased and biodegradable polyester composites combine the good mechanical and degradable properties of polyester, thereby providing an alternative for bone implant materials. Bone tissue engineering (BTE) accelerates bone defect repair by simulating the bone microenvironment.
View Article and Find Full Text PDFA deformable SIS/HA composite hydrogel coaxial scaffold promotes alveolar bone regeneration after tooth extraction.
Bioact Mater
April 2025
School and Hospital of Stomatology, Tianjin Medical University, Tianjin, 300070, China.
After tooth extraction, alveolar bone absorbs unevenly, leading to soft tissue collapse, which hinders full regeneration. Bone loss makes it harder to do dental implants and repairs. Inspired by the biological architecture of bone, a deformable SIS/HA (Small intestinal submucosa/Hydroxyapatite) composite hydrogel coaxial scaffold was designed to maintain bone volume in the socket.
View Article and Find Full Text PDFBiofabrication of anisotropic articular cartilage based on decellularized extracellular matrix.
Biofabrication
January 2025
Tissue Engineering + Biofabrication Laboratory, Department of Health Sciences & Technology, ETH Zürich, Otto-Stern-Weg 7, 8093 Zürich, Switzerland.
Tissue-engineered grafts that mimic articular cartilage show promise for treating cartilage injuries. However, engineering cartilage cell-based therapies to match zonal architecture and biochemical composition remains challenging. Decellularized articular cartilage extracellular matrix (dECM) has gained attention for its chondro-inductive properties, yet dECM-based bioinks have limitations in mechanical stability and printability.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!