A Comparative Evaluation of Time-dependent Changes on the Surface Hardness of Bulk Cure Composites: An Study.

Objectives: The objective of this study was to assess the surface hardness through Vickers hardness (VH) test of one conventional hybrid resin composites (Filtek Z350), compared with that of two bulk cure resin composites (SDR™, Tetric N Ceram®).

Materials And Methods: Twenty specimens of each material were prepared in cylindrical aluminum molds with an internal diameter of 5 mm and depth of 4 mm, 10 (incremental curing) and 10 (bulk curing).The surface of each specimen was covered with a transparent plastic matrix strip before light curing with conventional visible light for 40 seconds. The specimens thus obtained were stored in deionized water and transferred to an incubator at 37°C for 24 hours to simulate clinical conditions. After 24 hours, the microhardness of each specimen was measured using a Vickers indenter, with a load of 100 gm and dwell time of 15 seconds (HV 0.2/40).The specimens were further subjected to VH test in an interval of 7, 30, and 90 days. The data were subjected to statistical analysis-Student's t test, analysis of variance, and Tukey's test.

Results: The present study showed that SDR™ in bulk curing showed consistently greater value of hardness and was comparable to traditional incremental cured Filtek Z350, highlighting the advantages of the new SDR technology. Sarma A, Nagar P. A Comparative Evaluation of Time-dependent Changes on the Surface Hardness of Bulk Cure Composites: An Study. Int J Clin Pediatr Dent 2018;11(3):183-187.