A new processing route to produce Ultrafine-Grained Dual-Phase steel has been proposed, involving cold-rolling and subsequent intercritical annealing of a fibrous ferrite⁻martensite starting structure. Ultrafine-grained DP (UFG-DP) steel with an average ferrite grain size of about ~2.7 μm and an average martensite island size of ~2.9 μm was achieved. Tensile testing revealed superior mechanical properties (the ultimate tensile strength of 1267 MPa and uniform elongation of 8.2%) for the new DP steel in comparison with the fibrous DP steels. The superior mechanical properties are attributed to the influence of microstructure refinement on the work-hardening and fracture behavior.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6119992 | PMC |
| http://dx.doi.org/10.3390/ma11081399 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!