Influence of pre-heating and ceramic thickness on physical properties of luting agents.

Purpose: The objective of this in vitro study was to evaluate the influence of ceramic thickness and pre-heating of luting agents on their physical properties.

Materials And Methods: The materials RelyX Arc, RelyX Ultimate, RelyX Veneer, and Filtek Z350 Flow were handled at different temperatures (23°C or 54°C), inserted into matrix, and photoactivated through ceramic disks (0.75 mm or 1.5 mm). The following tests were performed ( n=8): degree of conversion, Knoop Hardness, cross-link density, water sorption, solubility, and ultimate tensile strength. Data were analyzed using three-way analysis of variance and Tukey's test (α=0.05).

Results: Regarding ceramic thickness, the thinnest ceramic resulted in higher values of Knoop Hardness ( p=0.027). The lowest temperature (23°C) resulted in a higher solubility ( p=0.0257), and water sorption ( p=0.0229) values. There was also statistical difference among the materials: RelyX Arc showed a higher degree of conversion and ultimate tensile strength, followed by RelyX Veneer, RelyX Ultimate, and Filtek Z350 Flow. For Knoop Hardness and cross-link density tests, RelyX Ultimate showed the highest values, followed by RelyX Arc, RelyX Veneer, and Filtek Z350 Flow. For water sorption and solubility, RelyX Veneer showed the highest values, followed by RelyX Arc, RelyX Ultimate, and Filtek Z350 Flow.

Conclusion: Pre-heating interfered with water sorption and solubility, whereas ceramic thickness only affected Knoop Hardness; the physical properties of the materials are dependent on their composition.