Purpose: To evaluate the effect of acidic challenge (AC) on the properties and bond stability of restorative materials to primary enamel and dentin.
Materials And Methods: One hundred twenty primary molars were assigned to 12 groups according to substrate (enamel or dentin), restorative material (composite, high-viscosity glass ionomer cement [HV-GIC] or resin-modified glass-ionomer cement [RM-GIC]), and immersion after restoration (control [saline solution/7 days] or AC [cola-based drink/5 min/3x per day/7 days]). Twenty-four hours after the restorative procedure, specimens were submitted to one of the proposed challenges. Half of the specimens were immediately subjected to the microshear bond strength test, and the other half after 12 months. To determine flexural strength flexural strength and superficial roughness (SR), 30 specimens were built up. After 24 h, the first measurement of SR from 10 specimens was performed. Specimens were then immersed in one of proposed challenges and SR was measured again. Subsequently, flexural strength testing was performed. Bond strength, surface roughness, and flexural strength data were subjected to ANOVA and Tukey's test.
Results: Composite showed the highest bond strengths compared to the others materials on both substrates. The storage period negatively influenced the bond strength only for composite groups in dentin. AC after restoration negatively influenced bond strength when the materials were evaluated in eroded dentin. AC affected the second SR measurement, showing increased SR for all restorative materials. AC did not affect flexural strength.
Conclusion: The acidic challenge jeopardizes the surface roughness and bond strength of restorations to eroded dentin.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.a40513 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Breaking the Ice: Hofmeister Effect-Inspired Hydrogen Bond Network Reconstruction in Hydrogel Electrolytes for High-Performance Zinc-Ion Batteries.
Small
December 2024
State Key Laboratory of Crystal Materials, Shandong University, Jinan, 250100, P. R. China.
Gel electrolytes have emerged as a promising solution for enhancing the performance of zinc-ion batteries (ZIBs), particularly in flexible devices. However, they face challenges such as low-temperature inefficiency, constrained ionic conductivity, and poor mechanical strength. To address these issues, this study presents a novel PAMCD gel electrolyte with tunable freezing point and mechanical properties for ZIBs, blending the high ionic conductivity of polyacrylamide with the anion interaction capability of β-cyclodextrin.
View Article and Find Full Text PDFSurface roughness and profile dataset of Ti6Al4V textured by laser ablation and spark erosion.
Data Brief
December 2024
Centro Universitário FEI, Avenida Humber de Alencar Castelo Branco, 3972, São Bernardo do Campo, 09850-901 São Paulo, Brazil.
The Ti6Al4V alloy is widely recognized for its extensive industrial applications, particularly in the aeronautics sector, due to its exceptional strength to-weight ratio and corrosion resistance. In this context, many industrial processes depend critically on surface area, topology, and roughness. A promising approach involves combining Ti6Al4V alloy with polymer composites, which offers significant potential for engineers to design parts that are not only high-performing but also environmentally friendly.
View Article and Find Full Text PDFHydrogen Bond Blueshifts in Nitrile Vibrational Spectra Are Dictated by Hydrogen Bond Geometry and Dynamics.
JACS Au
December 2024
Freie Universität Berlin, Physics Department, Experimental Molecular Biophysics, Arnimallee 14, 14195 Berlin, Germany.
Vibrational Stark effect (VSE) spectroscopy has become one of the most important experimental approaches to determine the strength of noncovalent, electrostatic interactions in chemistry and biology and to quantify their influence on structure and reactivity. Nitriles (C≡N) have been widely used as VSE probes, but their application has been complicated by an anomalous hydrogen bond (HB) blueshift which is not encompassed within the VSE framework. We present an empirical model describing the anomalous HB blueshift in terms of H-bonding geometry, i.
View Article and Find Full Text PDFBonding performance of universal adhesive systems to enamel - Effects of the acidic composition.
Dent Mater
December 2024
Graduate Program in Dentistry, School of Dentistry, Federal University of Rio Grande do Sul, Rua Ramiro Barcelos, Porto Alegre 2492, Brazil; Department of Conservative Dentistry, School of Dentistry, Federal University of Rio Grande do Sul, Rua Ramiro Barcelos, Porto Alegre 2492, Brazil. Electronic address:
Objectives: To evaluate the self-etch bonding potential of universal adhesive systems with varying acidic compositions by analyzing the wettability properties, topographical change, and microshear bond strength (µSBS) to enamel.
Methods: Eight universal adhesives were tested: All-Bond Universal (Bisco), Ambar Universal (FGM), Gluma Bond Universal (Kulzer), OptiBond Universal (Kerr), Peak Universal Bond (Ultradent), Prime&Bond Universal (Dentsply), Singlebond Universal (3 M ESPE), and Tetric N-Bond Universal (Ivoclar). Bovine incisors were prepared and treated with each adhesive according to the manufacturer's instructions.
Clean and sustainable extraction of gelatin: Effects of microwave and freeze-thaw on the crosslinking degree and hydrogen bond of fish skin collagen.
Food Chem
December 2024
College of Food Science, Southwest University, Chongqing 400715, China; Chongqing Key Laboratory of Speciality Food Co-Built by Sichuan and Chongqing, Chongqing 400715, China; Key Laboratory of Luminescence Analysis and Molecular Sensing (Southwest University), Ministry of Education, Chongqing 400715, China. Electronic address:
The traditional gelatin extraction methods (acid-base) may hinder to their green applications due to mass energy consumption and pollution. Herein, we constructed a clean and sustainable gelatin extraction method, investigated the molecular mechanism of microwave treatment (0-360 min) and freeze-thaw on the gelatin extraction from the perspective of the crosslinking degree and hydrogen bonds. Microwave (0-60 min) can improve the hydrolysis degree (DH) and expose more enzyme cleavage sites of collagen by destroying the intramolecular and intermolecular covalent crosslinking.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!