Marginal and internal fit of pre-sintered Co-Cr and zirconia 3-unit fixed dental prostheses as measured using microcomputed tomography.

Statement Of Problem: Limited information is available on the precision of new metal processing technologies.

Purpose: The purpose of this in vitro study was to evaluate the marginal and internal fit of pre-sintered cobalt-chromium (Co-Cr) and zirconia 3-unit fixed dental prostheses using x-ray microcomputed tomography.

Material And Methods: Three-unit fixed dental prostheses were prepared on metal dies (N=12) using a typodont model from the maxillary first premolar to the first molar. A standardized preparation with a 1.2-mm chamfer (360 degrees) and a 2-mm occlusal reduction was prepared on abutment teeth. The dies were scanned and divided into 2 groups to receive the fixed dental prostheses (n=6) made of pre-sintered Co-Cr and pre-sintered zirconia. Each framework was seated on its cast, and marginal and internal discrepancies were measured at 9 points, starting from the most distal point from the pontic for the maxillary first premolar and the first molar (points 1-4, mesial; point 5, occlusal; points 6-9, distal) of each abutment tooth using microcomputed tomography. The data were analyzed using the Levene test, t test, and ANOVA (α=.05).

Results: When overall mean discrepancy values were compared, no significant difference was observed between pre-sintered Co-Cr and pre-sintered zirconia (P=.085). Discrepancy values for points 1, 2, and 3 were significantly different for pre-sintered Co-Cr and pre-sintered zirconia, with the lowest mean values for point 1 and the highest for point 5. On the abutment tooth basis, for the maxillary first premolar and the first molar, a significant difference was found only in points 6 (P<.001) and 8 (P<.003) for both materials. When the discrepancies for the maxillary first premolar were considered for pre-sintered Co-Cr and pre-sintered zirconia, the mean values were significantly different only at points 1 (P<.001), 2 (P=.007), and 3 (P=.003) and were smaller for pre-sintered zirconia. For the tooth the first molar, a significant difference was observed at point 2 (P=.002) and point 3 (P=.008) for both materials, where the mean values were higher for pre-sintered Co-Cr than for pre-sintered zirconia. The pairwise comparison between points showed a significant difference between measurement points within each material (P<.05). The increase in values between points 1 and 5 was evident for both pre-sintered Co-Cr and pre-sintered zirconia materials.

Conclusions: Three-unit fixed dental prostheses made of pre-sintered Co-Cr or zirconia showed similar marginal and internal discrepancy values, with the highest discrepancy values at the occlusal region in both the first premolar and first molar.