Nanopowder synthesis of novel Sn(II)-imprinted poly(dimethyl vinylphosphonate) by ultrasound-assisted technique: Adsorption and pre-concentration of Sn(II) from aqueous media and real samples.

In this research, a novel Sn(II)-imprinted poly(dimethyl vinylphosphonate) nanopowder (Sn(II)-IPDMVPN) was prepared using Sn, dimethyl vinylphosphonate, azobis isobutyronitril and ethylene glycol dimethacrylate as the template, ligand, initiator and cross linker, respectively. The non-imprinted poly(dimethyl vinylphosphonate) nanopowder (NIPDMVPN) was also synthesized utilizing the same procedure without using SnCl·2HO in order to compare the results with the Sn(II)-IPDMVPN. The structure, morphology and composition of the products were characterized by XRD, SEM, EDX, XRF, BET, FT-IR and NMR techniques. Some experimental conditions including pH, eluent concentration and sample volume were optimized to maximize Sn(II) adsorption by the Sn(II)-IPDMVPN. It was found that the optimum conditions are pH = 5, 1.00 M of HNO as eluent and sample volume up to 50 mL. The results obtained by ICP-MS indicated that the Sn(II)-IPDMVPN had much higher adsorption capacity for Sn(II) ions (about threefold) than the NIPDMVPN. The applicability of the Sn(II)-IPDMVPN was also investigated in three different real samples. Under the best experimental conditions, the calibration graphs were linear in the range of 0.19-90 μg L with a coefficient of determination (R) of 0.990. The detection limit was calculated to be 0.06 μg L. The relative standard deviation (RSD) for six replicate measurements of Sn(II) at 1.00 ng mL was determined to be 1.8%. The results showed that the Sn(II)-IPDMVPN-ICP-MS is a very simple, rapid, sensitive and efficient method for the determination of Sn(II) ions in water samples.