Evaluation of Sandblasting on Mechanical Properties and Cell Response of Bioactive Glass Infiltrated Zirconia.

This study investigated the mechanical properties and initial cell response of bioactive glass infiltrated zirconia before and after sandblasting. One hundred zirconia specimens were divided into the following four groups: untreated zirconia (ZR), sandblasted zirconia (ZS), glass infiltrated zirconia (ZG), and sandblasted glass infiltrated zirconia (ZGS). Surface roughness, biaxial flexural strength, hardness and osteoblast cells proliferation were evaluated. ZGS group showed a slight decrease in hardness. However it has improvement in flexural strength (686.2 MPa). After sandblasting, the ZGS group had the highest surface roughness (R a = 1.24 μm) with enhanced osteoblast cells response. Our results indicated that sandblasting method can improve the mechanical properties of bioactive glass infiltrated zirconia with better osteoblast cell response. This new surface is promising for zirconia dental implant application in the future.