Debris extrusion and foraminal deformation produced by reciprocating instruments made of thermally treated NiTi wires.

To evaluate the amount of apically extruded debris, percentage of foraminal enlargement and apical foramen (AF) deformation that occurred during root canal preparation with different reciprocation systems: Reciproc, WaveOne (M-Wire), and ProDesign R (Shape Memory Technology Wire) at two different working lengths (WLs): 0.0 and 1.0 mm beyond the AF. The AF of 120 root canals in 60 mesial roots of mandibular molars were photographed with stereomicroscope and randomly assigned into four groups: manual, Reciproc (REC), WaveOne (WO), and ProDesign R (PDR); subsequently, they were further subdivided according to the WL (n=15). Teeth were instrumented, coupled to a dual collecting chamber, and then another photograph of each AF was captured. Extrusion was analysed by determining the weight of extruded debris. Each AF diameter was measured in pre- and post-instrumentation images to determine deformation, which was analysed, and afterwards the final format of AFs was classified (circular/oval/deformed). We found no significant differences when analysing each system at different WLs. When considering each WL, REC and WO showed highest extrusion values (P<.05); for AF enlargement, differences were observed only for WO, when it was used beyond the AF; differences were observed among M-Wire groups beyond the AF (P<.05). AF deformation was observed in all groups; PDR showed the lowest AF deformation values at both WLs; M-Wire groups showed 50% strain beyond the AF. Authors concluded that beyond the apical limit, the alloy and taper are important aspects when considering extrusion and deformation.