Objectives: The aim of this study was to evaluate the cyclic and torsional fatigue resistance of the reciprocating single-file systems Reciproc Blue 25.08 (VDW GmbH, Munich, Germany), Prodesign R 25.06 (Easy Dental Equipment, Belo Horizonte, Brazil), and WaveOne Gold 25.07 (Dentsply/Tulsa Dental Specialties, Tulsa, OK, USA).
Materials And Methods: Sixty reciprocating instruments of the systems Reciproc Blue R25 (RB #25 .08 taper), Prodesign R (PDR #25 .06 taper), and WaveOne Gold (WOG #25 .07 taper) (n = 20) were used. Cyclic fatigue resistance testing was performed by measuring the time to failure in an artificial stainless steel canal with a 60° angle of curvature and a 5-mm radius located 5 mm from the tip (n = 10). The torsional test (ISO 3630-1) evaluated the torque and angle of rotation at failure of new instruments (n = 10) in the portion 3 mm from the tip. The fractured surface of each fragment was also observed using scanning electron microscopy (SEM). In addition, a supplementary examination was performed to measure the cross-sectional area of each instrument 3 and 5 mm from the tip. The data were analyzed using one-way ANOVA and Tukey's test, and the level of significance was set at 5%.
Results: The cyclic fatigue resistance values of PDR 25.06 were significantly higher (P < 0.05). RB 25.08 showed higher fatigue resistance than WOG 25.07 (P < 0.05). The torsional test showed that PDR 25.06 had lower torsional strength (P < 0.05). No differences were observed between RB 25.08 and WOG 25.07 (P > 0.05). PDR 25.06 showed higher angular rotation values than RB 25.08 and WOG 25.07 (P < 0.05). RB 25.08 presented higher angular rotation than WOG 25.07 (P < 0.05). The cross-sectional area analysis showed that PDR 25.06 presented the smallest cross-sectional areas at 3 and 5 mm from the tip (P < 0.05).
Conclusion: PDR 25.06 presented the highest cyclic fatigue resistance and angular rotation until fracture compared to RB 25.08 and WOG 25.07. In addition, RB 25.08 and WOG 25.07 had higher torsional strength than PDR 25.06.
Clinical Relevance: In endodontic practice, thermally treated reciprocating instruments have been used for the root canal preparation of curved and constricted canals; therefore, these instruments should present high flexibility and suitable torsional strength to minimize the risk of instrument fracture.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1007/s00784-017-2295-8 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Characterization of Fatigue Properties of Fiber-Reinforced Polymer Composites Based on a Multiscale Approach.
Polymers (Basel)
January 2025
Department of Mechanical Engineering, Hanyang University, 222 Wangsimri-ro, Seongdong-gu, Seoul 04763, Republic of Korea.
This study presents a methodology for characterizing the constituent properties of composite materials by back-calculating from the laminate behavior under fatigue loading. Composite materials consist of fiber reinforcements and a polymer matrix, with the fatigue performance of the laminate governed by the interaction between these constituents. Due to the challenges in directly measuring the properties of individual fibers and the polymer matrix, a reverse-engineering approach was employed.
View Article and Find Full Text PDFExperimental Investigation on Macroscopic and Microscopic Mechanical Properties of Geopolymer-Stabilized Macadam.
Materials (Basel)
January 2025
School of Civil Engineering, Central South University, Changsha 410075, China.
Geopolymer, as a promising inorganic binding material, holds potential for use in constructing base layers for highway pavements. This study aims to evaluate the mechanical properties of geopolymer-stabilized macadam (GSM) at both the micro- and macro-scale by a series of tests, demonstrating that high-Ca GSM is a high-quality material for pavement base layers. The results demonstrated that GSM exhibits outstanding mechanical and fatigue properties, significantly surpassing those of cement-stabilized macadam (CSM).
View Article and Find Full Text PDFStrain-Controlled Thermal-Mechanical Fatigue Behavior and Microstructural Evolution Mechanism of the Novel Cr-Mo-V Hot-Work Die Steel.
Materials (Basel)
January 2025
School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang 471023, China.
In response to the intensifying competition in the mold market and the increasingly stringent specifications of die forgings, the existing 55NiCrMoV7 (MES 1 steel) material can no longer meet the elevated demands of customers. Consequently, this study systematically optimizes the alloy composition of MES 1 steel by precisely adjusting the molybdenum (Mo) and vanadium (V) contents. The primary objective is to significantly enhance the microstructure and thermal-mechanical fatigue performance of the steel, thereby developing a high-performance, long-life hot working die steel designated as MES 2 steel.
View Article and Find Full Text PDFEffect of Inert Gas Cover on the Static and Fatigue Behavior of AA6061-T6 Aluminum Alloy Friction Stir Spot Lap-Shear Welds.
Materials (Basel)
January 2025
Department of Mechanical Engineering, Faculty of Engineering, University of Isfahan, Isfahan 817467344, Iran.
Friction stir spot welding (FSSW) technology relies on the generation of frictional heat during the rotation of the welding tool in contact with the workpiece as well as the stirring effect of the tool pin to produce solid-state spot joints, especially for lightweight materials. Although FSSW offers significant advantages over traditional fusion welding, the oxidation of the interfacial bond line remains one of the most challenging issues, affecting the quality and strength of the joint under both static and cyclic loading conditions. In this experimental study, inert argon gas was employed to surround the joint, aiming to prevent or minimize the formation of the interfacial oxides.
View Article and Find Full Text PDFAccelerated Method for Determining the Fatigue Limit of Trabecular Bone.
Materials (Basel)
January 2025
Faculty of Mechanical Engineering, Bydgoszcz University of Science and Technology, Kaliskiego 7, 85-796 Bydgoszcz, Poland.
This paper presents an experimental method for estimating the fatigue limit of trabecular bone using a single trabecular bone sample, the microstructural parameters of which were determined by microCT. Fatigue tests were carried out using the Locati method, with stepwise increasing load amplitude. The fatigue limits of the trabecular structures were determined experimentally in accordance with Miner's law of fatigue damage accumulation, based on the parameters of the reference S-N curve taken from the literature.