Metal-organic frameworks (MOFs) have been widely used to prepare corresponding porous metal oxides via thermal treatment. However, high temperature treatment always leads to obtained metal oxides with a large crystallite size, thus decreasing their specific surface area. Different from the conventional complete thermal decomposition of MOFs, herein, using Ce-MOF as a demonstration, we choose partial thermal decomposition of MOF, followed by selective etching to prepare porous/hollow structured ceria because of the poor stability of Ce-MOF under acidic conditions. Compared with the ceria derived from complete thermal decomposition of Ce-MOF, the as-prepared ceria is demonstrated to be a good support for copper oxide species during the CO oxidation catalytic reaction. Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and hydrogen temperature-programmed reduction (H-TPR) analysis revealed that the as-prepared ceria is favorable for strengthening the interaction between the ceria and loaded copper oxide species. This work is expected to open a new, simple avenue for the synthesis of metal oxides from MOFs via partial thermal decomposition.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1021/acsami.7b11916 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Insights into semi-continuous synthesis of iron oxide nanoparticles (IONPs) via thermal decomposition of iron oleate.
Discov Nano
January 2025
Particle Engineering Centre, Department of Chemical Engineering, Norwegian University of Science and Technology, Trondheim, 7491, Norway.
The increasing demand for magnetic iron oxide nanoparticles (IONPs) in biomedicine necessitates efficient and scalable production methods. Thermal decomposition offers excellent tailoring of the particle properties but its discontinuous batch-operation is restricting scale-up and industrial application. To overcome these challenges, several studies have demonstrated semi-continuous thermal decomposition by slowly injecting the precursor, though only half of them produce magnetite IONPs and even fewer use iron oleate precursors.
View Article and Find Full Text PDFVacancy-Activated B-Doping for Efficient 2e- Oxygen Reduction through Suppressing H2O2 Decomposition at High Overpotential.
Angew Chem Int Ed Engl
January 2025
China University of Petroleum East China, State Key Laboratory of Heavy Oil Processing, 66 The Yangtze River West Road, 266580, Qingdao, CHINA.
The production of hydrogen peroxide (H2O2) through two-electron oxygen reduction reaction (2e- ORR) has emerged as a more environmentally friendly alternative to the traditional anthraquinone method. Although oxidized carbon catalysts have intensive developed due to their high selectivity and activity, the yield and conversion rate of H2O2 under high overpotential still limited. The produced H2O2 was rapidly consumed by the increased intensity of H2O2 reduction, which could ascribe to decomposition of peroxide radicals under high voltage in the carbon catalyst.
View Article and Find Full Text PDFDesign of Polydopamine@iron Oxide-Coated Ammonium Perchlorate Core-Shell Composites for Enhancing the Combustion Performance of HTPB-Based Propellants.
Langmuir
January 2025
School of Environment and Safety Engineering, North University of China, Taiyuan 030051, China.
An ammonium perchlorate (AP) composite system with double-coating encapsulation based on the interfacial polymerization behavior of dopamine (DA) in Pickering emulsions was designed to enhance the combustion performance of HTPB-based propellants. The composite system proved highly effective in mitigating the agglomeration issues associated with iron oxide nanoparticles (FeO NPs) as catalysts, with the AP exhibiting superior performance compared to the composite comprising pure FeO NPs. The results of the thermal decomposition experiments showed that the HTD temperature of AP@PDA@FeO was reduced to 318.
View Article and Find Full Text PDFTracing the Origins of Calendar Aging in Si-Containing Lithium-Ion Batteries.
Nano Lett
January 2025
Department of Thermal Science and Energy Engineering, University of Science and Technology of China (USTC), Hefei, Anhui 230026, China.
Lithium-ion batteries (LIBs) with silicon/graphite composite (Si/C) anodes are still facing the challenge of unsatisfactory calendar life, and the specific impact of Si on this issue is largely unknown. Herein, the calendar aging behaviors are quantified across scales and explored in a top-down manner. Batteries with 10 wt % Si/C anodes suffer a 4-fold decrease in the overall lifetime and a 4-5-fold increase in irreversible anode loss.
View Article and Find Full Text PDFPolymer Biodegradation in Aquatic Environments: A Machine Learning Model Informed by Meta-Analysis of Structure-Biodegradation Relationships.
Environ Sci Technol
January 2025
Department of Civil and Environmental Engineering, Case Western Reserve University, Cleveland, Ohio 44106, United States.
Polymers are widely produced and contribute significantly to environmental pollution due to their low recycling rates and persistence in natural environments. Biodegradable polymers, while promising for reducing environmental impact, account for less than 2% of total polymer production. To expand the availability of biodegradable polymers, research has explored structure-biodegradability relationships, yet most studies focus on specific polymers, necessitating further exploration across diverse polymers.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!