Preparation and characterization of CrFeWTiO photoanodes and their photoelectrochemical activities for water splitting.

The chemical bath deposition (CBD) method was successfully applied to prepare WTiO nanotube arrays co-deposited with chromium, iron and chromium-iron nanoparticles. Various methods have been used in the characterization of synthetic co-deposited nanostructures. WTiO nanotubes can keep the nanotubular structures at low iron concentration in the CBD solution, as indicated by our FESEM results. Iron and chromium can be applied to improve the absorption capability of the WTiO nanotubes for the visible-light, according to the UV-Vis results. Based on the photoelectrochemical performance and photocatalytic hydrogen evolution characteristics of the CrFeWTiO catalysts, the co-deposited nanoparticles contribute to the improvement in the photocatalytic efficiency. The best photocatalytic activity was shown by the CrFeWTiO-1 sample formed by immersion in a CBD solution containing 0.08 M ClCl·6HO + 0.02 M FeCl·6HO. The hydrogen evolution reaction of the new photocatalysts showed that their photocatalytic activity was very stable. A facile method has been developed in this study for the synthesis of high performance co-deposited photocatalysts with excellent stability and reliability in photoelectrochemical water splitting. A stable and high photocatalytic activity for hydrogen evolution in the absence of a Pt co-catalyst was exhibited by the novel CrFeWTiO compounds prepared.