The surface of polymethylmethacrylate (PMMA) is vulnerable to indentation by hard objects that may contribute to abrade the material surface and subject it to wear. This phenomenon promotes an increase in the surface roughness leading to microbial colonisation which can endanger the general health of wearers and damage the intra-oral prosthesis. The aim of this study is to investigate the effect of three different nanocryl coating agents (Easy Glaze, G-Coat Plus and Formulation XP) on surface roughness and thickness of PMMA material after a simulating cleaning process utilizing an electric toothbrush and three different dentifrices (pastes and immersion). Acrylic uncoated discs were used as a control group. The results showed that the G-Coat Plus coating agent had less changes in the surface roughness and thickness layer whereas the immersion cleaner revealed less abrasion effect compared with the paste cleaners which could be considered the most suitable cleaner to provide lower abrasivenes and good removal of organic debris. However, using nanofilled sealants did not demonstrate significant improvement in reducing surface roughness p ⟩ 0.05. Nevertheless, it could provide some protection against wearing to the acrylic resin surface during tooth brushing and may provide better resistance to microbial colonisation.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1922/EJPRD_01679Fathi11 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Enhancing Bioactivity of Titanium-Based Materials Through Chitosan Based Coating and Calcitriol Functionalization.
Ann Biomed Eng
January 2025
Department of Biomedical Engineering, Yildiz Technical University, Esenler, 34220, Istanbul, Türkiye.
Titanium (Ti)-based materials are favored for hard tissue applications, yet their bioinertness limits their success. This study hypothesizes that functionalizing Ti materials with chitosan nano/microspheres and calcitriol (VD) will enhance their bioactivity by improving cellular activities and mineralization. To test this, chitosan particles were applied uniformly onto Ti surfaces using electrophoretic deposition (EPD) at 20 V for 3 minutes.
View Article and Find Full Text PDFThe impact of bleaching using 15% carbamide peroxide on surface properties of CAD-CAM composite structures.
Sci Rep
January 2025
Division of Dentistry, School of Medical Sciences, The University of Manchester, Manchester, M13 9PL, UK.
This study aims to evaluate the effects of the home bleaching method on the surface microhardness and surface roughness of both polished and unpolished CAD-CAM resin composite materials. A polymer-infiltrated ceramic network (PICN) block, Enamic (VE), along with four resin composite blocks (RCB) (Grandio [GN], Lava™ Ultimate [LV], BRILLIANT Crios [B], and Cerasmart [CS]), were prepared to dimensions of 14 mm × 12 mm × 2 mm and were categorized into unpolished and polished groups (n = 4). Microhardness measurements were conducted using a Vickers microhardness tester (300 gf load for 20 s) at various time points: before home bleaching, after home bleaching with 15% Opalescence for 8 h and for 56 h, 24 h after bleaching, and one month after bleaching.
View Article and Find Full Text PDFSustainability metrics targeted optimization and electric discharge process modelling by neural networks.
Sci Rep
January 2025
Center for Automation and Robotics, CSIC-Universidad Politécnica de Madrid, Arganda del Rey, Madrid, 28500, Spain.
Aluminium and its alloys, especially Al6061, have gathered significant interest among researchers due to its less density, great durability, and high strength. Due to their lightweight properties, the precise machining of these alloys can become expensive through conventional machining operations for intricate products. Therefore, non-traditional machining such as electric discharge machining (EDM) can potentially be opted for the cutting of Al6061.
View Article and Find Full Text PDFOptimizing thermal and thermal-alkaline pretreatments for polylactic acid biodegradation by Amycolatopsis orientalis and Amycolatopsis thailandensis.
Bioresour Technol
January 2025
BioTeC+ - Chemical and Biochemical Process Technology and Control, Department of Chemical Engineering, KU Leuven, Gebroeders De Smetstraat 1, 9000 Gent, Belgium.
Environmental pollution from packaging, has led to a need for sustainable alternatives. This study investigates the biodegradation of polylactic acid (PLA) by Amycolatopsis orientalis and Amycolatopsis thailandensis after thermal and thermal-alkaline pretreatments. The biodegradation was assessed based on weight loss, CO evolution, carbon balance analysis and scanning electron microscopy (SEM).
View Article and Find Full Text PDFInfluence of sterilization and exposure to the Ringer's solution on physicochemical properties of nitrocarburized 316 LVM steel.
Acta Bioeng Biomech
September 2024
Faculty of Materials Science and Engineering, Warsaw University of Technology, Warsaw, Poland.
The aim of the study was to investigate the influence of the nitrocarburizing process carried out in low temperature plasma using the active screen at 440 °C on the structure and physicochemical properties of the 316LVM steel. In the paper, results of micro-structure and phase composition of the layers, roughness, and surface wettability, potentiodynamic pitting corrosion resistance, penetration of ions into the solution as well as biological tests were present. The studies were conducted for the samples of both mechanically polished and nitrocarburized surfaces, after sterilization, and exposure to the Ringer's solution.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!