Purpose: To evaluate in a randomized clinical evaluation the 3-year clinical durability of a one-step universal adhesive and compare it intraindividually with a 2-step self-etch adhesive in Class II restorations.
Materials And Methods: Each of 57 participants (mean age 58.3 years) received at least two extended Class II restorations that were as similar as possible. The cavities in each of the 60 individual pairs of cavities were randomly distributed to the 1-step universal adhesive (All-Bond Universal: AU) and the control 2-step self-etch adhesive (Optibond XTR: OX). A low shrinkage composite (Aelite LS) was used for all restorations, which were evaluated using slightly modified USPHS criteria at baseline and 1, 2, and 3 years.
Results: 114 Class II restorations were evaluated at three years. Eight restorations, 3 AU and 5 OX, failed during the follow-up, resulting in 94.7% (AU) and 91.2% (OX) success rates (p > 0.05). Annual failure rates were 1.8% and 2.9%, respectively.The main reason for failure was composite fracture.
Conclusion: Class II composite restorations placed with a 1-step universal adhesive showed good short-term efficacy.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.a38867 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Cell-Based Glioma Models for Anticancer Drug Screening: From Conventional Adherent Cell Cultures to Tumor-Specific Three-Dimensional Constructs.
Cells
December 2024
School of Medicine and Life Sciences, Far Eastern Federal University, 690922 Vladivostok, Russia.
Gliomas are a group of primary brain tumors characterized by their aggressive nature and resistance to treatment. Infiltration of surrounding normal tissues limits surgical approaches, wide inter- and intratumor heterogeneity hinders the development of universal therapeutics, and the presence of the blood-brain barrier reduces the efficiency of their delivery. As a result, patients diagnosed with gliomas often face a poor prognosis and low survival rates.
View Article and Find Full Text PDFCoating Agents for Resin Composites: Effect on Color Stability, Roughness, and Surface Micromorphology Subjected to Brushing Wear.
Oper Dent
January 2025
*Roberta Tarkany Basting, DDS, MSc, PhD, Professor, Restorative Dentistry Department, Faculdade São Leopoldo Mandic, São Paulo, Brazil.
This study evaluated the influence of six resin composite coating agents on color stability and surface roughness after toothbrushing abrasion. Discs (Ø6 mm x 2 mm) of nanofilled resin composite (Filtek Z350XT) were prepared for application of coating agents (n=10): control (absence), two surface sealants (PermaSeal and BisCover LV), two adhesive systems (Scotchbond Multi-Purpose Adhesive/3M Oral Care and Single Bond Universal), and two modeling liquids (Modeling Resin and Composite Wetting Resin). CIELab*, WID, and color change (ΔEab, ΔE00, and ΔWID) were analyzed at baseline, after finishing and polishing, after application of coating agents, after coffee staining (simulating 30 days and one year of staining), and after toothbrushing abrasion.
View Article and Find Full Text PDFQuasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material.
J Vis Exp
December 2024
School of Engineering and Materials Science, Queen Mary University of London.
Article Synopsis
- The study evaluates the fracture strength of 1 mm-thick CAD/CAM occlusal veneers made from lithium disilicate (LD) and resin nanoceramics (RNC) to assess their viability in dental restoration.
- Using a novel testing protocol, the RNC group demonstrated a significantly higher load-bearing capacity compared to the LD group, indicating better durability under stress.
- Both materials experienced similar crack patterns during testing, emphasizing the importance of understanding mechanical properties for ensuring the longevity of dental restorations.
Bond strength comparison of chemically activated hard reline materials on CAD-CAM milled and conventional heat-polymerized PMMA denture bases.
J Prosthet Dent
January 2025
Assistant Professor, Department of Prosthodontic, College of Dental Medicine, Rangsit University, Phatum Thani, Thailand. Electronic address:
Statement Of Problem: Comprehensive data are needed on the performance of chemically activated, chairside hard reline materials when used with computer-aided design and computer-aided manufacturing (CAD-CAM) milled polymethyl methacrylate (PMMA) denture bases and conventionally processed bases. This lack of data affects decisions regarding the chairside reline material to be used for improving the fit and retention of relined complete dentures.
Purpose: The purpose of this in vitro study was to evaluate and compare the shear bond strength (SBS) of 3 chemically activated, chairside hard reline materials on CAD-CAM milled and conventional heat-polymerized PMMA denture bases.
The effect of different adhesive strategies and diamond burs on dentin bond strength of universal resin cements.
Clin Oral Investig
January 2025
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo, Japan.
Objectives: To evaluate the shear bond strength (SBS) of universal cements (UCs) to dentin prepared with different diamond burs using various adhesive strategies.
Materials And Methods: One-hundred-twenty molars were prepared to expose the mid-coronal dentin. The teeth were divided into two groups according to diamond bur preparations: coarse and super-fine grit burs.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!