Gelation and Retrogradation Mechanism of Wheat Amylose.

The flow behavior, dynamic viscoelasticity, and optical rotation of aqueous solutions of wheat amylose were measured using a rheogoniometer and a polarimeter. The amylose solutions, at 25 °C, showed shear-thinning behavior at a concentration of 1.2%, but plastic behavior at 1.4 and 1.6%, the yield values of which were estimated to be 0.6 and 1.0 Pa, respectively. The viscosity of the wheat amylose increased a little with increase in temperature up to 10 or 20 °C at 1.2% or 1.4 and 1.6%, which was estimated to be a transition temperature. The elastic modulus increased with increase in concentration, and increased with increasing temperature up to 20, 25 and 30 °C, which was estimated to be a transition temperature, respectively, then decreased gradually but stayed at a large value even at high temperature (80 °C). A very low elastic modulus of the wheat amylose was observed upon addition of urea (4.0 M) and in alkaline solution (0.05 M NaOH) even at low temperature. The optical rotation of wheat amylose solution increased a little with decreasing temperature down to 25 °C, then increased rapidly with further decrease in the temperature. The mode of gelation mechanism of amylose molecules, which was previously proposed, was confirmed and a retrogradation mechanism of wheat amylose was proposed.