The effect of Fe2O3 crystal phases on their performance in CO2 hydrogenation was studied. α-Fe2O3 crystal was prepared by precipitation method from Fe(NO3)3·9H2O and (NH4)2CO3, and γ-Fe2O3 was prepared by grinding Fe(NO3)3·9H2O and L(+)-Tartaric acid in agate mortar completely. The crystal phases of Fe2O3 influence the distribution of promoter Zn, K and Cu on catalysts. The dispersity of K on γ-Fe2O3 surface is higher than α-Fe2O3. On the contrary, Cu and Zn are more dispersive on α-Fe2O3 surface than γ-Fe2O3. The catalyst in γ-Fe2O3 phase is easily reduced relative to the catalyst in α-Fe2O3 phase. The former presents higher CO2 conversion and C2+ hydrocarbon selectivity than the latter in CO2 hydrogenation.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC5555619 | PMC |
| http://journals.plos.org/plosone/article?id=10.1371/journal.pone.0182955 | PLOS |
Publication Analysis
Top Keywords
Similar Publications
Heteroleptic "open ruthenocene" for deposition of Ru films from the gas phase.
Dalton Trans
January 2025
Johnson Matthew Technology Centre, Blounts Court Rd., Sonning Common, RG4 9NH, UK.
A volatile heteroleptic open ruthenocene has been synthesised and characterised by NMR and single crystal X-ray diffraction. Using this compound as a precursor and oxygen as a co-reactant, a highly conductive Ru film has been deposited on Si with native oxide at 220 °C. Under the same deposition conditions, the film thickness obtained with the new compound has almost doubled compared to its homoleptic analogue.
View Article and Find Full Text PDFSurface-Confined Disordered Hydrogen Bonds Enable Efficient Lithium Transport in All-Solid-State PEO-Based Lithium Battery.
Angew Chem Int Ed Engl
January 2025
Fuzhou University College of Chemical Engineering, College of Chemical Engineering, CHINA.
Polyethylene oxide (PEO)-based electrolytes are essential to advance all-solid-state lithium batteries (ASSLBs) with high safety/energy density due to their inherent flexibility and scalability. However, the inefficient Li+ transport in PEO often leads to poor rate performance and diminished stability of the ASSLBs. The regulation of intermolecular H-bonds is regarded as one of the most effective approaches to enable efficient Li+ transport, while the practical performances are hindered by the electrochemical instability of free H-bond donors and the constrained mobility of highly ordered H-bonding structures.
View Article and Find Full Text PDFSurface Template Realizing Oriented Perovskites for Highly Efficient Solar Cells.
Adv Mater
January 2025
Institute of Functional Nano & Soft Materials (FUNSOM), Jiangsu Key Laboratory of Advanced Negative Carbon Technologies, Soochow University, Suzhou, 215123, China.
Formamidinium lead iodide (FAPbI) perovskite films, ensuring optically active phase purity with uniform crystal orientation, are ideal for photovoltaic applications. However, the optically active α-FAPbI phase is easy to degrade into δ-phase due to numerous defects within randomly oriented films. Here, a "quasi-2D" perovskite template is pre-deposited on the film surface within the crystallization process based on the two-step preparation technology, which directly induced pure and highly orientated crystallization of α-FAPbI across the downward growth process.
View Article and Find Full Text PDFNucleation-Controlled Crystallization of Chiral 2D Perovskite Single Crystal Thin Films for High-Sensitivity Circularly Polarized Light Detection.
Adv Mater
January 2025
MOE Key Laboratory of Macromolecular Synthesis and Functionalization, International Research Center for X Polymers, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, China.
2D Dion-Jacobson (DJ) chiral perovskite materials exhibit significant promise for developing high-performance circularly polarized light (CPL) photodetectors. However, the inherently thick nature of DJ-phase 2D perovskite single crystal limits their ability to differentiate CPL photons with the two opposite polarization states. In addition, the growth of DJ-phase perovskite single crystal thin films (SCTFs) has proven challenging due to the strong interlayer electronic coupling.
View Article and Find Full Text PDFDesigning Robust Quasi-2D Perovskites Thin Films for Stable Light-Emitting Applications.
Adv Mater
January 2025
Department of Physics, SUNY University at Buffalo, Buffalo, NY, 14220, USA.
Quasi-2D perovskite made with organic spacers co-crystallized with inorganic cesium lead bromide inorganics is demonstrated for near unity photoluminescence quantum yield at room temperature. However, light emitting diodes made with quasi-2D perovskites rapidly degrade which remains a major bottleneck in this field. In this work, It is shown that the bright emission originates from finely tuned multi-component 2D nano-crystalline phases that are thermodynamically unstable.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!