This study examined the effects of 3 mol % yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) ceramic surface treatments on the tensile bond strength and surface characteristics of enamel. To measure the tensile bond strength, the 3Y-TZP and tooth specimens were manufactured in a mini-dumbbell shape and divided into four groups based on the type of 3Y-TZP surface treatment: polishing (P), 110 µm alumina sandblasting (S), 110 µm alumina sandblasting combined with selective infiltration etching (SS), and 110 µm alumina sandblasting combined with MDP (10-methacryloyloxydecyl dihydrogen phosphate)-containing silane primer (SP). After surface treatment, the surface roughness, wettability, and surface changes were examined, and the tensile bond strength was measured. The mean values (from lowest to highest) for tensile bond strength (MPa) were as follows: P, 8.94 ± 2.30; S, 21.33 ± 2.00; SS, 26.67 ± 4.76; and SP, 31.74 ± 2.66. Compared to the P group, the mean surface roughness was significantly increased, and the mean contact angle was significantly decreased, while wettability was increased in the other groups. Therefore, surface treatment with 110 µm alumina sandblasting and MDP-containing silane primer is suitable for clinical applications, as it considerably improves the bond strength between 3Y-TZP and enamel.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC5512524 | PMC |
| http://dx.doi.org/10.3390/ma9080702 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Scanning electron microscopy analysis of metallic and aesthetic bracket meshes before and after debonding.
Korean J Orthod
January 2025
Materials Research Institute, National Autonomous University of Mexico, Mexico City, Mexico.
Objective: To study the influence of bracket base meshes on shear bond strength and observe them using a scanning electron microscopy (SEM) before and after debonding.
Methods: Ninety brackets were divided into nine groups of 10 samples each: G1-Alexander, G2-Mini Sprint Brackets, G3-In-Ovation R CCO, G4-Gemini SL Self-Ligating Bracket, G5-Classic mini 2G Stylus, G6-Gemini Metal Brackets, G7-Clarity Advanced, G8-Crystall-Ize, and G9-Ceramic Series Flexx 2G. Groups G1 to G6 and G7 to G9 consisted of metallic and aesthetic brackets, respectively.
Weak Covalent Bonds and Mechanochemistry for Synergistic Self-Strengthening of Elastomers.
J Am Chem Soc
January 2025
State Key Laboratory of Fine Chemicals, Frontier Science Center for Smart Materials, Dalian University of Technology, West Campus, 2# Linggong Road, Dalian 116024, China.
The macroscopic properties of elastomers are intimately linked to their molecular reactivity and mechanisms. Here, we propose a new strategy for designing strengthening materials based on the synergy of weak covalent bonds and mechanochemistry. After mechanical treatment, the failure strength and toughness of the elastomer increased from 2.
View Article and Find Full Text PDFEnhancing gel and 3D printing performance of lipid-enhanced skipjack tuna (Katsuwonus pelamis) surimi via Pickering high internal phase emulsion.
Food Res Int
February 2025
Hainan Engineering Research Center of Aquatic Resources Efficient Utilization in South China Sea, Key Laboratory of Food Nutrition and Functional Food of Hainan Province, Key Laboratory of Seafood Processing of Haikou, College of Food Science and Technology, Hainan University, Hainan 570228, China; Collaborative Innovation Center of Provincial and Ministerial Co-Construction for Marine Food Deep Processing, Dalian Polytechnic University, Dalian 116034, China. Electronic address:
This study explored the effect of lactoferrin (LF)-stabilized fish oil Pickering high internal phase emulsions (HIPPEs) on the gel property and 3D printing performance of skipjack tuna surimi compared with directly added fish oil. Based on the various environmental stress stability, HIPPEs could remain relatively stable when added to surimi gels. The luminance and whiteness of skipjack tuna surimi gel were significantly (p < 0.
View Article and Find Full Text PDFShort dentin etching with universal adhesives: effect on bond strength and gingival margin adaptation.
BMC Oral Health
January 2025
Conservative Department, Faculty of Dentistry, Kafr Al Sheikh University, Kafr Al Sheikh, Egypt.
Background: Short dentin etching, a relatively recent technique, aims to improve resin-dentin bonding by preserving hydroxyapatite crystals within the collagen spaces. This study explores short dentin etching's potential in mitigating over-etching issues in deep proximal dentin/cementum margins, an aspect not previously investigated. This study evaluates the microtensile bond strength (μTBS) and marginal adaptation of two universal adhesives using different etch-and-rinse strategies (15-second and 3-second etching) and self-etch strategies, both immediate and post-thermal cycling and mechanical loading.
View Article and Find Full Text PDFGingival margin interfacial microleakage, staining, and push-out strengths of gingival colored composite resins in denture bases.
J Prosthet Dent
January 2025
Professor, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil. Electronic address:
Statement Of Problem: Staining at the gingival margin could impact denture longevity, but the behavior of gingival colored composite resins (GCCs) in this area remains unclear.
Purpose: This in vitro study evaluated surface staining, microleakage, and push-out bond strength at the gingival margin of artificial teeth, comparing two consistencies of GCCs with two resin base materials.
Material And Methods: Specimens included artificial teeth (Ivostar; Ivoclar AG) and two acrylic resin base materials: conventional (Ondacryl; Clássico) and high-impact (Diamond D; Keystone Industries) (n=300).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!