Preparation and Application of Immobilized Surfactant-Modified PANi-CNT/TiO₂ under Visible-Light Irradiation.

Hydrothermally and sol-gel-synthesized immobilized surfactant-modified polyaniline-carbon nanotubes/TiO₂ (PANi-CNT/TiO₂) photocatalysts were prepared and their application in the degradation of diethyl phthalate (DEP) under visible light at 410 nm was investigated in this sturdy. To improve the dispersion of nanoparticles and the transfer of electrons, the TiO₂ surface was modified with both sodium dodecyl sulfate (SDS) and functionalized carbon nanotubes (CNT-COOH and CNT-COCl). With the addition of PANi, which was increased from 1%-5%, the adsorption edge of the prepared photocatalysts shifted to 442 nm. The SDS linked the PANi polymers to achieve a thickness of coating of the film of up to 314-400 nm and 1301-1600 nm for sol-gel hydrolysis and hydrothermally-synthesized photocatalysts, respectively. An appropriate film thickness would extend the transfer path of the electrons and inhibit the recombination of the electrons and the electron-holes. The photo-degradation performance of DEP by the hydrothermally-synthesized photocatalysts was better than those by sol-gel hydrolysis. The results revealed that the hydroxyl radicals were the key oxidant in the degradation of DEP using hydrothermally-synthesized PANi-CNT/TiO₂ photocatalysts. The morphology and functional groups of the raw materials of photocatalysts were characterized and a comparison of photocatalytic activity with other TiO₂-based photocatalysts was also provided.