In order to achieve a high-quality joint between SiO/SiO and metals, it is necessary to address the poor wettability of SiO/SiO and the high residual stress in SiO/SiO-Nb joint. Here, we simultaneously realize good wettability and low residual stress in SiO/SiO-Nb joint by combined method of HF etching treatment and Finite Element Analysis (FEA). After etching treatment, the wettability of E-SiO/SiO was improved, and the residual stress in the joint was decreased. In order to better control the quality of joints, efforts were made to understand the relationship between surface structure of E-SiO/SiO and residual stress in joint using FEA. Based on the direction of FEA results, a relationship between residual stress, surface structure and joint property in the brazed joints were investigated by experiments. As well the FEA and the brazing test results both realized the high-quality joint of E-SiO/SiO-Nb and the shear strength of the joint reached 61.9 MPa.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC5482827PMC
http://dx.doi.org/10.1038/s41598-017-04531-wDOI Listing

Publication Analysis

Top Keywords

residual stress
24
joint
9
structure joint
8
joint property
8
high-quality joint
8
stress sio/sio-nb
8
sio/sio-nb joint
8
etching treatment
8
stress joint
8
surface structure
8

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!