Activation-Dependent Breathing in a Flexible Metal-Organic Framework and the Effects of Repeated Sorption/Desorption Cycling.

A non-interpenetrated metal-organic framework with a paddle-wheel secondary building unit has been activated by direct thermal evacuation, guest exchange with a volatile solvent, and supercritical CO drying. Conventional thermal activation yields a mixture of crystalline phases and some amorphous content. Exchange with a volatile solvent prior to vacuum activation produces a pure breathing phase with high sorption capacity, selectivity for CO over N and CH , and substantial hysteresis. Supercritical drying can be used to access a guest-free open phase. Pressure-resolved differential scanning calorimetry was used to confirm and investigate a systematic loss of sorption capacity by the breathing phase as a function of successive cycles of sorption and desorption. A corresponding loss of sample integrity was not detectable by powder X-ray diffraction analysis. This may be an important factor to consider in cases where flexible MOFs are earmarked for industrial applications.