High Temperature Synthesis of Single-Component Metallic Nanoparticles.

Nanoparticles (NPs) dispersed within a conductive host are essential for a range of applications including electrochemical energy storage, catalysis, and energetic devices. However, manufacturing high quality NPs in an efficient manner remains a challenge, especially due to agglomeration during assembly processes. Here we report a rapid thermal shock method to synthesize well-dispersed NPs on a conductive fiber matrix using metal precursor salts. The temperature of the carbon nanofibers (CNFs) coated with metal salts was ramped from room temperature to ∼2000 K in 5 ms, which corresponds to a rate of 400,000 K/s. Metal salts decompose rapidly at such high temperatures and nucleate into metallic nanoparticles during the rapid cooling step (cooling rate of ∼100,000 K/s). The high temperature duration plays a critical role in the size and distribution of the nanoparticles: the faster the process is, the smaller the nanoparticles are, and the narrower the size distribution is. We also demonstrated that the peak temperature of thermal shock can reach ∼3000 K, much higher than the decomposition temperature of many salts, which ensures the possibility of synthesizing various types of nanoparticles. This universal, , high temperature thermal shock method offers considerable potential for the bulk synthesis of unagglomerated nanoparticles stabilized within a matrix.