Purpose: To evaluate the effects of tribochemical silica coating and different 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing primers on the shear bond strength (SBS) of orthodontic metal brackets to yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) surfaces.
Materials And Methods: One hundred ninety polished Y-TZP specimens were randomly assigned to 19 groups (n = 10): 30 specimens were used for surface analyses after polishing with 600-grit silicon carbide paper, airborneparticle abrasion with 50-μm alumina (A), or tribochemical silica coating (CoJet [C]); 160 specimens were used in SBS testing of orthodontic metal brackets to Y-TZP after alumina airborne-particle abrasion or tribochemical silica coating and application of either ESPE-Sil (S) (ASn, ASa, CSn, CSa), Alloy Primer (AP) (AAPn, AAPa, CAPn, CAPa), Clearfil Ceramic Primer (CP) (ACPn, ACPa, CCPn, CCPa), or Scotchbond Universal (U) (AUn, AUa, CUn, CUa) and either stored in water for 24 h (non-aged, n) or thermocycled 5000 times (aged, a). The surface analyses and SBSs were statistically analyzed with ANOVA and Tukey's tests.
Results: Both mechanically treated surfaces had significantly greater surface roughness and surface free energy than did the polished surfaces. The type of primer and aging significantly affected the bond strength. Among the thermocycled specimens, the AAPa, AUa, and CCPa groups showed the greatest SBS.
Conclusion: After alumina airborne-particle abrasion, the application of Alloy Primer, Clearfil Ceramic Primer, or Scotchbond Universal provided stable bonding to Y-TZP ceramics. After tribochemical silica coating, however, only Clearfil Ceramic Primer produced a durable bond to Y-TZP ceramics.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.a37724 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Graphene Mitigates Nanoscale Tribochemical Wear of Silica Glass in Water.
Small
December 2024
Department of Materials Science and Engineering, Indian Institute of Technology Delhi, Hauz Khas, New Delhi, 110016, India.
Despite the ubiquitous use of glasses, their simultaneous susceptibility toward scratch-induced defects and atmospheric hydration deteriorates their mechanical and chemical durability. Here, it is demonstrated that the deposition of a few-layer graphene provides unprecedented wear resistance to silica glass in aqueous conditions. To this extent, nanoscale scratch tests are carried out on graphene-glass surfaces via contact-mode atomic force microscopy with chemically inert and reactive tips.
View Article and Find Full Text PDFThe Effect of Immediate Dentin Sealing Using Different Universal Adhesives on the Bond Strength of Pretreated Monolithic Zirconia to Dentin and Microscopic Morphological Alterations.
Microsc Res Tech
December 2024
Department of Restorative Dentistry, Marmara University Faculty of Dentistry, Istanbul, Turkey.
This study evaluated the effects of immediate dentin sealing (IDS) using different universal adhesives on microtensile bond strength (μTBS) of pretreated monolithic translucent tetragonal polycrystalline zirconia-based CAD/CAM restoration to dentin and microscopic morphological alterations. Mid-coronal dentin were obtained from 32 human molars and randomly allocated into 8 groups according to the presence/absence of IDS, universal adhesives for IDS (Single Bond Universal/SBU, Clearfil Quick Bond/CUQ, Optibond Universal/OBU) and zirconia surface pretreatments (tribochemical silica coating-30 μm CoJet particles/TSC, sandblasting-50 μm AlO/SB): Group TSC, Group TSC+SBU, Group TSC+CUQ, Group TSC+OBU, Group SB, Group SB+SBU, Group SB+CUQ, Group SB+OBU. CAD/CAM restorations (Lava Plus High Translucency Zirconia Disc) were produced, luted, and subjected to 10.
View Article and Find Full Text PDFEffects of primer components of silane and 10-methacryloyloxydecyl dihydrogen phosphate on resin bonding to tribochemical silica-coated highly translucent zirconia.
Clin Oral Investig
November 2024
Department of Applied Prosthodontics, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1, Sakamoto, Nagasaki, 852-8588, Japan.
Objectives: To assess the influence of different primer compositions-silane (S), 10-methacryloyloxydecyl dihydrogen phosphate (MDP), and the combination of silane and MDP (S + MDP)-on the bonding performance of MDP-free and MDP-containing resin cements to highly translucent zirconia.
Materials And Methods: Tribochemical silica-coated zirconia plates were pretreated with one of three experimental primers, S, MDP, or S + MDP, with untreated specimens serving as controls. Subsequently, these plates were bonded to stainless-steel rods using either two MDP-free or two MDP-containing resin cements.
A Comprehensive Review of Techniques for Enhancing Zirconia Bond Strength: Current Approaches and Emerging Innovations.
Cureus
October 2024
Dentistry, Ministry of Health, Al Bahah, SAU.
The increasing use of zirconia in dental restorations necessitates a comprehensive understanding of effective bonding techniques to ensure long-term clinical success. Zirconia's unique chemical composition presents challenges in achieving a durable bond as it lacks the glass phase necessary for traditional etching and silanization processes. This review evaluates current methods and emerging innovations for enhancing zirconia bond strength to resin cements.
View Article and Find Full Text PDFThe purpose of this study was to determine the most effective method for bonding composite resin to artificially aged amalgam. A spherical amalgam alloy was triturated and condensed by hand into cylindrical plastic molds (6 mm in diameter and 4 mm in height) to create 90 specimens, which were then aged for 2 weeks in closed plastic containers at 23°C. The amalgam surfaces underwent 1 of 3 surface treatments (n = 30 per treatment): (1) air particle abrasion (APA) with 50-μm aluminum oxide particles applied with a force of 45 psi from a 10-mm distance, followed by rinsing with deionized water for 60 seconds; (2) APA following the same protocol with subsequent application of a metal primer (Alloy Primer); or (3) coating with 30-μm silica (CoJet) at a force of 45 psi from a 10-mm distance until the surface turned black.