3D Printing of Aniline Tetramer-Grafted-Polyethylenimine and Pluronic F127 Composites for Electroactive Scaffolds.

Electroactive hydrogel scaffolds are fabricated by the 3D-printing technique using composites of 30% Pluronic F127 and aniline tetramer-grafted-polyethylenimine (AT-PEI) copolymers with various contents from 2.5% to 10%. The synthesized AT-PEI copolymers can self-assemble into nanoparticles with the diameter of ≈50 nm and display excellent electroactivity due to AT conjugation. The copolymers are then homogeneously distributed into 30% Pluronic F127 solution by virtue of the thermosensitivity of F127, denoted as F/AT-PEI composites. Macroscopic photographs of latticed scaffolds elucidate their excellent printability of F/AT-PEI hydrogels for the 3D-printing technique. The conductivities of the printed F/AT-PEI scaffolds are all higher than 2.0 × 10 S cm , which are significantly improved compared with that of F127 scaffold with only 0.94 × 10 S cm . Thus, the F/AT-PEI scaffolds can be considered as candidates for application in electrical stimulation of tissue regeneration such as repair of muscle and cardiac nerve tissue.