The Electrochemical Response of Single Crystalline Copper Nanowires to Atmospheric Air and Aqueous Solution.

In this paper, single crystalline copper nanowires (CuNWs) have been electrochemically grown through anodic aluminum oxide template. The environmental stability of the as-obtained CuNWs in both 40% relative humidity (RH) atmosphere and 0.1 m NaOH aqueous solution has been subsequently studied. In 40% RH atmosphere, a uniform compact Cu O layer is formed as a function of exposure time following the logarithmic law and epitaxially covers the CuNW surfaces. It is also found that the oxide layers on CuNWs are sequentially grown when subjected to the cyclic voltammetry measurement in 0.1 m NaOH solution. An epitaxially homogeneous Cu O layer is initially formed over the surface of the CuNW substrates by solid-state reaction (SSR). Subsequently, the conversion of Cu O into epitaxial CuO based on the SSR takes place with the increase of applied potential. This CuO layer is partially dissolved in the solution forming Cu(OH) , which then redeposited on the CuNW surfaces (i.e., dissolution-redeposition (DR) process) giving rise to a mixed polycrystalline CuO/Cu(OH) layer. The further increase of applied potential allows the complete oxidation of Cu O into CuO to form a dual-layer structure (i.e., CuO inner layer and Cu(OH) outer layer) with random orientations through an enhanced DR process.