Synthesis of monodisperse spherical core-shell SiO-SrAlSiO: Eu phosphors by hydrothermal homogeneous precipitation method.

Nanocrystalline SrAlSiO :Eu phosphor layers were coated on nonaggregated, monodisperse and spherical SiO particles using a hydrothermal homogeneous precipitation. After annealing at 1100 °C, core-shell SiO@SrAlSiO :Eu particles were obtained. They were characterized with x-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy and photoluminescence techniques. XRD analysis confirmed the formation of SiO @SrAlSiO :Eu particles; it indicated that the SrAlSiO :Eu shells on SiO particles consisted of hexagonal crystallites. The core-shell phosphors obtained are well-dispersed submicron spherical particles with a narrow size distribution. The thickness of the coated layer is approximately 20-40 nm. Under ultraviolet excitation (361 nm), the particles emit blue light at about 440 nm due to the Eu ions in their shells.