Objectives: This study evaluated the microtensile bond strength (μTBS) of a resin composite bonded to bleached enamel as a function of bleaching conditions.
Materials And Methods: The whiteness hydrogen peroxide (HP) bleaching agent containing 35% HP was applied to the central incisors' facial enamel surface and irradiated as follows: No treatment (G1; control); no light (G2); light-emitting diode, the 40s (G3); diode laser, the 20s (G4); and neodymium:yttrium aluminum garnet laser, 20s (G5). A Variolink II resin composite structure was then built up incrementally on the surface. The teeth were sectioned into three 1.2 mm × 1.2 mm wide "I"-shaped sections. The specimens were then subjected to microtensile testing at a crosshead speed of 1 mm/min. Data were analyzed using one-way ANOVA (α =0.05) followed by the Tukey Honestly Significant Difference post-hoc test. The fractured surfaces were observed with a stereomicroscope at × 100 magnification.
Results: One-way ANOVA revealed no statistical differences among the groups (P > 0.05). No differences appeared between the groups bonded 14 days after bleaching (P > 0.05). Mean μTBS values (MPa) were as follows: 22.05 ± 5.01 (G1); 19.6 ± 5.6 (G2); 19.3 ± 5.4 (G3); 20.08 ± 2.08 (G4); and 18.1 ± 4.8 (G5). Many adhesive failures occurred at the bleached and irradiated enamel surfaces.
Conclusion: The various irradiation treatments following the application of the whiteness HP bleaching agent to enamel did not significantly reduce the μTBS within a 14-day period.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4103/1119-3077.178909 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Clinical performance of minimally invasive full-mouth rehabilitation using different materials and techniques for patients with moderate to severe tooth wear: a systematic review and meta-analysis.
Clin Oral Investig
January 2025
Department of Prosthodontics, Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou, 310000, Zhejiang, China.
Objective: To evaluate short, mid and long-term clinical outcomes and patients' satisfaction of minimally invasive full-mouth rehabilitation using different materials and techniques for patients with moderate to severe tooth wear. Furthermore, materials were analyzed to identify their influences on clinical results.
Materials And Methods: Search was conducted in PubMed, Cochrane Central Register of Controlled Trial, Embase, Web of science and Scopus until December 19, 2024.
Mechanical properties of modern restorative "bioactive" dental materials - an in vitro study.
Sci Rep
January 2025
Department of General Dentistry, Medical University of Lodz, 251 Pomorska Str, Lodz, 92-213, Poland.
This study aimed at assessing the mechanical properties and degradation of commercial bioactive materials. The bioactive materials (Activa Bioactive Restorative, Beautifil Flow Plus F00, F03, Predicta Bulk Bioactive) and composite resin Filtek Supreme Flow were submitted to flexural and diametral tensile strength tests (FS, DTS), modulus of elasticity (ME) evaluation, and analysis of aging in 70% ethanol and saliva on their hardness and sorption. The results for DTS ranged from 33.
View Article and Find Full Text PDFComparing Sectional and Total Dentin Bond Strengths of Three Endodontic Sealers after Using the Single-cone Obturation Technique: An Study.
J Contemp Dent Pract
October 2024
College of Dentistry, Ajman University, Ajman P.O. Box 346, United Arab Emirates; Department of Endodontic, Faculty of Dentistry, Mansoura University, Egypt, Orcid: https://orcid.org/0000-0003-3391-5306.
Aim: This study aimed to investigate and compare the total and sectional bond strengths of three endodontic sealers when used with the single-cone obturation technique.
Materials And Methods: Forty-five human maxillary central incisors were prepared and divided into three groups according to the type of endodontic sealer: Group I (Gutta-percha/AH Plus Jet), group II (Gutta-percha/GuttaFlow 2), and group III (RealSeal/RealSeal SE). All canals were filled with the single-cone technique.
Comparative Evaluation of Surface Roughness and Color Stability of Polyetheretherketone with Conventional Interim Prosthetic Materials: An Study.
J Contemp Dent Pract
October 2024
Department of Prosthodontics, Government Dental College, Kozhikode, Kerala, India, Orcid: https://orcid.org/0000-0003-1456-3851.
Aim: The aim of this study was to compare the surface roughness and color stability of polyetheretherketone (PEEK) with those of conventional interim prosthetic materials like polymethylmethacrylate, bis-acrylic composite, and rubberized diurethane dimethacrylate, following immersion in solutions of varying pH value.
Materials And Methods: A total of 320 circular discs with 10 mm diameter and 2 mm height were divided based on the fabrication ( = 80)-group A: polymethylmethacrylate; group B: bis-acrylic composite; group R: rubberized diurethane; and group P: hot-pressed PEEK-and were subjected to baseline measurement of roughness ( = 40) and color ( = 40) using 3D profilometer and UV-Vis spectrophotometer, respectively. Later, 10 samples from each group were immersed in distilled water, black coffee, green tea, and Pepsi, respectively, for 120 days, and measurements of roughness and color were repeated.
Effect of Mushroom, Ozone Gas, and Their Combination as Pretreatment Materials on the Bond Strength of Resin Composite to Dentin.
J Contemp Dent Pract
October 2024
Department of Dental Biomaterials, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt, Orcid: https://orcid.org/0000-0002-3420-4146.
Aim: To assess the effect of mushrooms, ozone gas, and their combination as cavity disinfectants on the bonding strength of composite to dentin.
Materials And Methods: The study was conducted on 40 sound premolar teeth randomly divided into four groups. Group I: control group, Group II: mushroom group, Group III: Ozone group, and Group IV: mushroom + ozone gas (combination) group.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!