Calcium phosphate, in the form of amorphous hydroxyapatite, precipitates out of neutral water solutions containing calcium and phosphate ions in the form of small agglomerates of 18 μm average size. When Hydron Blue dye (HB) is added, the insoluble particles gradually agglomerate further to 50 μm sizes. However, the removal capacity of hydroxyapatite for the dye is increased when the calcium phosphate nucleates and forms in the presence of dye. When coprecipitates form, the particules average 20 μm size and contain up to 60% organic matter. Nascent calcium phosphate particles have strong capacity for Hydron Blue dye removal. Thus smaller calcium phosphate particles increase the amount of dye molecules in water pollution control.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.jenvman.2016.09.039 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Morrey Award 2023: radial head donor plug for capitellum osteochondral autograft transfer: a cadaveric biomechanical analysis.
JSES Int
November 2024
Department of Orthopaedic Surgery, University of Iowa, Iowa City, IA, USA.
Background: Limitations to using the knee as donor cartilage include cartilage thickness mismatch and donor site morbidity. Using the radial head as donor autograft for capitellar lesions may allow for local graft harvest without distant donor site morbidity. The purpose of this study is to demonstrate the feasibility of performing local osteochondral autograft transfer from the nonarticular cartilaginous rim of the radial head to the capitellum.
View Article and Find Full Text PDFCalcium phosphate formation and deposition in ischemic neurons.
PLoS One
January 2025
Biomedical Engineering Department, Northwestern University, Evanston, IL, United States of America.
Ischemic stroke causes acute brain calcium phosphate (CaP) deposition, a process involving primarily the injured neurons. Whereas the adverse impact of CaP deposition on the brain structure and function has been recognized, the underlying mechanisms remain poorly understood. This investigation demonstrated that the neuron-expressed, plasma membrane-associated Ca2+-binding proteins annexin (Anx) A2, AnxA5, AnxA6, and AnxA7 contributed to neuronal CaP deposition in the mouse model of ischemic stroke.
View Article and Find Full Text PDFThe impact of glidants on the rheological properties of active pharmaceutical ingredients: A study of conventional and alternative flow enhancers.
Int J Pharm
January 2025
Laboratory of Pharmaceutical Technology, Department of Pharmaceutics, Ghent University, Ottergemsesteenweg 460, B-9000 Ghent, Belgium.
Nowadays, most of the newly developed active pharmaceutical ingredients (APIs) consist of cohesive particles with a mean particle size of <100μm, a wide particle size distribution (PSD) and a tendency to agglomerate, therefore they are difficult to handle in continuous manufacturing (CM) lines. The current paper focuses on the impact of various glidants on the bulk properties of difficult-to-handle APIs. Three challenging powders were included: two extremely cohesive APIs (acetaminophen micronized (APAPμ) and metoprolol tartrate (MPT)) which previously have shown processing issues during different stages of the continuous direct compression (CDC)-line and a spray dried placebo (SD) powder containing hydroxypropylmethyl cellulose (HPMC), known for its sub-optimal flow with a high specific surface area (SSA) and low density.
View Article and Find Full Text PDFDual-stimuli-responsive nanoparticles for the co-delivery of small molecules to promote neural differentiation of human iPSCs.
Nanoscale
January 2025
Department of Biomedical Engineering, Sogang University, Seoul 04107, Korea.
The differentiation of human induced pluripotent stem cells (hiPSCs) into neural progenitor cells (NPCs) is a promising approach for the treatment of neurodegenerative diseases and regenerative medicine. Dual-SMAD inhibition using small molecules has been identified as a key strategy for directing the differentiation of hiPSCs into NPCs by regulating specific cell signaling pathways. However, conventional culture methods are time-consuming and exhibit low differentiation efficiency in neural differentiation.
View Article and Find Full Text PDFFabrication and characterization of 3D-printed polymeric-based scaffold coated with bioceramic and naringin for a potential use in dental pulp regeneration (in vitro study).
Int Endod J
January 2025
Restorative and Aesthetic Dentistry Department, College of Dentistry, University of Baghdad, Baghdad, Iraq.
Aim: 3D-printed scaffolds loaded with healing directed agents could be employed for better treatment outcome in regenerative dentistry. The aim of this study was to fabricate and characterize simple 3D-printed poly lactic acid (PLA) scaffolds coated with nanoHydroxyapatite (nHA), Naringin (NAR), or their combination, and testing their morphological, chemical, mechanical, antibacterial, biocompatible and bioactive properties.
Methodology: Two variants pore sizes, 300 and 700 μm, of 3D-printed PLA disc scaffolds measuring (10 × 1 mm) were fabricated.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!