Objective: To determine and compare the micro topographic characteristics of dental implants submitted to different surface treatments, using scanning electron microscopy (SEM).
Materials And Methods: Implants were divided into 7 groups of 3 specimens each, according to the surface treatment used: group 1: Osseotite, BIOMET 3i; group 2: SLA surface, Institut Straumann AG; group 3: Oxalife surface, Tree-Oss implant; group 4: B&W implant surface; group 5: Q-implant surface; group 6: ML implant surface; group 7: RBM surface, Rosterdent implant. The surfaces were examined under SEM (Carl Zeiss FE-SEM-SIGMA). Image Proplus software was used to determine the number and mean diameter of pores per area unit (mm). The data obtained were analyzed with the Mann-Whitney test. A confocal laser microscope (LEXT-OLS4100 Olympus) was used to conduct the comparative study of surface roughness (Ra). Data were analyzed using Tukey's HSD test.
Results: The largest average pore diameter calculated in microns was found in group 5 (3.45 µm+/-1.91) while the smallest in group 7 (1.47µm+/-1.29). Significant differences were observed among each one of the groups studied (p<0.05). The largest number of pores/mm(2) was found in group 2 (229343) and the smallest number in group 4 (10937). Group 2 showed significant differences regarding the other groups (p<0.05). The greatest roughness (Ra) was observed in group 2 (0.975µm+/-0.115) and the smallest in group 4 (0.304µm+/-0.063). Group 2 was significantly different from the other groups (p<0.05).
Conclusion: The micro topography observed in the different groups presented dissimilar and specific features, depending on the chemical treatment used for the surfaces..
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4892131 | PMC |
| http://dx.doi.org/10.2174/1874210601610010139 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Preclinical evaluation of zirconium-89 labeled anti-Trop2 antibody-drug conjugate (Trodelvy) for imaging in gastric cancer and triple-negative breast cancer.
Eur J Nucl Med Mol Imaging
January 2025
Departments of Radiology and Medical Physics, University of Wisconsin - Madison, Madison, WI, 53705, USA.
Purpose: Trophoblast cell-surface antigen 2 (Trop2) is overexpressed in various solid tumors and contributes to tumor progression, while its expression remains low in normal tissues. Trop2-targeting antibody-drug conjugate (ADC), sacituzumab govitecan-hziy (Trodelvy), has shown efficacy in targeting this antigen. Leveraging the enhanced specificity of ADCs, we conducted the first immunoPET imaging study of Trop2 expression in gastric cancer (GC) and triple-negative breast cancer (TNBC) models using Zr-labeled Trodelvy ([Zr]Zr-DFO-Trodelvy).
View Article and Find Full Text PDFCrystalline lens power and astigmatism calculation in myopia by swept-source optical coherence tomography: A pilot study.
Graefes Arch Clin Exp Ophthalmol
January 2025
National Clinical Research Center for Ocular Diseases, Eye Hospital, Wenzhou Medical University, 618# Fengqi East Road, Hangzhou, 310000, Zhejiang, China.
Purpose: To calculate the crystalline lens power and astigmatism, as well as their changes following cycloplegia, in individuals with myopia using swept-source optical coherence tomography (SS-OCT).
Methods: Participants were divided into two groups according to axial length (AL). Crystalline lens parameters, including power, lens thickness (LT), anterior chamber depth (ACD), and astigmatism, were measured with SS-OCT and analysed before and after cycloplegia.
Baricitinib Provides Significant Improvements in Quality of Life and Functioning in Adults with Moderate-to-Severe Atopic Dermatitis with Baseline Body Surface Area ≤ 40% and Severe Itch.
Dermatol Ther (Heidelb)
January 2025
Department of Dermatology, University of Tsukuba, Tsukuba, Japan.
Introduction: Patients with moderate-to-severe atopic dermatitis (AD), a body surface area (BSA) of ≤ 40%, and an itch numerical rating scale (NRS) score of ≥ 7 ("BARI itch dominant") have been characterized as an important group to consider for the oral janus kinase (JAK) 1/2 inhibitor baricitinib (BARI). Herein we aim to evaluate quality of life (QoL) and functioning outcomes in adult patients with BSA ≤ 40% and itch NRS ≥ 7 at baseline (BL) who received BARI 4 mg in the topical corticosteroid (TCS) combination trial BREEZE-AD7.
Materials: BREEZE-AD7 was a randomized, double-blind, placebo-controlled, parallel-group outpatient study involving adult patients with moderate-to-severe AD who received once-daily placebo or 2-mg or 4-mg BARI in combination with TCS for 16 weeks.
Comparison of Hydrogen Bonded Organic Framework with Reduced Graphene Oxide-Pd Based Nanocatalyst: Which One Is More Efficient for Entrapment of Nitrophenol Pollutants?
Langmuir
January 2025
Prof. Rashidi Laboratory of Organometallic Chemistry & Material Chemistry, Department of Chemistry, College of Science, Shiraz University, Shiraz, 7194684795, Iran.
In this study, a Pd nanoparticles@hydrogen-bonded organic framework (Pd NPs@HOF) thin film was fabricated at the toluene-water interface. The HOF was formed through the interaction of trimesic acid (TMA) and melamine (Mel) in the water phase, while Pd(0) was produced from the reduction of [PdCl(cod)] in the organic phase. The as-synthesized Pd NPs@HOF thin film was demonstrated to be an effective catalyst for the selective reduction of -nitrophenol and -nitrophenol to -aminophenol and -aminophenol.
View Article and Find Full Text PDFRegulating Interphase Chemistry by Targeted Functionalization of Hard Carbon Anode in Ester-based Electrolytes for High-Performance Sodium-Ion Batteries.
Angew Chem Int Ed Engl
January 2025
Harbin Institute of Technology, School of Chemistry and Chemical Engineering, No. 92, West Dazhi Street, 150001, Harbin, CHINA.
Commercial hard carbon (HC) anode suffers from unexpected interphase chemistry rooted in the parasitic reactions between surface oxygen-functional groups and ester-based electrolytes. Herein, an innovative strategy is proposed to regulate interphase chemistry by tailoring targeted functional groups on the HC surface, where highly active undesirable oxygen-functional groups are skillfully converted into a Si-O-Si molecular layer favorable for anchoring anions. Then, an inorganic/organic hybrid solid electrolyte interphase with low interfacial charge transfer resistance and enhanced cycling durability is constructed successfully.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!