Different pulse modes of Er:YAG laser irradiation: effects on bond strength achieved with self-etching primers.

Objective: The aim of this study was to compare the effects of different pulse modes of Er:YAG laser on shear bond strength (SBS) of orthodontic brackets bonded with self-etching primers (SEP) and phosphoric acid etching.

Materials And Methods: A total of 120 human mandibular third molars were randomly assigned to 3 groups of 40 specimens depending on the bonding procedure to be used. The groups were divided into two subgroups according to the pulse mode of the erbium-doped yttrium aluminum garnet (Er:YAG) laser irradiation as medium-short pulse (MSP) mode and quantum-square pulse (QSP) mode at 120 mJ, 10 Hz, 1.2 W. In each subgroup, the mesio- or distobuccal tooth surfaces were randomly assigned as experimental or control sides. After surface preparation with different modes of Er:YAG laser on experimental side, whole buccal tooth surfaces were treated with phosphoric acid etching or two different SEPs. Then metallic brackets were bonded with Transbond XT (3 M Unitek, Monrovia, CA, USA) or Kurasper F (Kuraray, Okayama, Japan). SBS values and the amount of adhesive remaining on the tooth after debonding were assessed. One-way analysis of variance (ANOVA) was used to evaluate the changes in mean SBS between groups resulting from laser etching, followed by post hoc test of Tukey.

Results: There were statistically significant differences between the experimental and control sides of all groups (p < 0.05).

Conclusion: Laser etching with QSP and MSP modes increases the SBS of metallic brackets and Er:YAG laser irradiation with QSP mode increases the SBS of SEPs.