Department of Production Technology, Madras Institute of Technology, Anna University, Chennai, Tamil Nadu, India.
Published: April 2016
AI Article Synopsis
Article Abstract
Objectives: The aim of this study was to investigate the role of deep cryogenic treatment (DCT) on the cyclic fatigue resistance and cutting efficiency of martensitic shape memory (SM) nickel-titanium (NiTi) rotary endodontic instruments.
Materials And Methods: Seventy-five HyFlex(®) CM instruments were randomly divided into three groups of 25 each and subjected to different DCT (-185° C) conditions based on soaking time: DCT 24 group: 24 h, DCT 6 group: 6 h, and control group. Each group was randomly subdivided for evaluation of cyclic fatigue resistance in custom-made artificial canals (n = 15) and cutting efficiency in plexiglass simulators (n = 10). The cyclic fatigue resistance was measured by calculating the number of cycles to failure (NCF) and cutting efficiency was measured using the loss of weight method.
Results: Increase in NCF of instruments in DCT 24 group was highly significant (P < 0.01; Tukey's honest significant difference). There was no difference in weight loss of plexiglass simulators in all the groups (P > 0.05; one-way analysis of variance). In conclusion, deep dry cryogenic treatment with 24 h soaking time significantly increases the cyclic fatigue resistance without affecting the cutting efficiency of SM NiTi endodontic instruments.
Materials And Methods: Seventy-five HyFlex(®) CM instruments were randomly divided into three groups of 25 each and subjected to different DCT (-185° C) conditions based on soaking time: DCT 24 group: 24 h, DCT 6 group: 6 h, and control group. Each group was randomly subdivided for evaluation of cyclic fatigue resistance in custom-made artificial canals (n = 15) and cutting efficiency in plexiglass simulators (n = 10). The cyclic fatigue resistance was measured by calculating the number of cycles to failure (NCF) and cutting efficiency was measured using the loss of weight method.
Results: Increase in NCF of instruments in DCT 24 group was highly significant (P < 0.01; Tukey's honest significant difference). There was no difference in weight loss of plexiglass simulators in all the groups (P > 0.05; one-way analysis of variance). In conclusion, deep dry cryogenic treatment with 24 h soaking time significantly increases the cyclic fatigue resistance without affecting the cutting efficiency of SM NiTi endodontic instruments.