The objective of this study was to evaluate the effect of passive or active phosphoric acid (PA) application after hydrofluoric acid (HA) treatment on the microshear bond strength of lithium disilicate. Thirty ceramic discs were made with IPS Emax 2 (10 mm thick and 10 mm diameter). The specimens were divided into 3 groups, A: 9.6% HA application; AF: 9.6% HA application + cleaning with 37% PA in passive mode and AFF: 9.6% HA application + cleaning with 37% PA in active mode. For the microshear test, four tygons (0.9 mm diameter and 0.2 mm high) were filled with resin cement (RelyX Ultimate) and placed on the ceramic disks. After testing, the fracture modes were examined under scanning electron microscopy. Data were analyzed by one-way ANOVA and Tukey's post test (α=0.05). The bond strength values were significantly higher in Group AFF (11.0±2.5 MPa) compared with group A (8.1±2.6 MPa) (p<0.002). AF group was not statistically different (9.4±2.5 MPa) from Group A. It was concluded that the active application of 37% PA after 9.6% HA increases the microshear bond strength values between the resin cement and lithium disilicate ceramic.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1590/0103-6440201600428 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Hydrogen Evolution Reaction in Borophene: Puckering Mechanism and the Role of Coordination Number.
ACS Omega
January 2025
Department of New Energy Science and Engineering, Xiamen University Malaysia, Sepang 43900, Malaysia.
Using the free energy of hydrogen adsorption (Δ ) as the indicator, five borophene phases are previously shown to possess high catalytic activity for the hydrogen evolution reaction (HER). On these borophene phases, we investigate the role of the coordination number (CN = 4, 5, 6) of the adsorption sites and the puckering of the adsorption site. CN is discovered to have a profound effect on the Δ distribution, charge, and puckering height () of adsorption sites.
View Article and Find Full Text PDFPrimary Dentin Conditioning with Methylene Blue Activated Photodynamic Therapy, Phytic Acid, and Er,Cr:YSGG to Resin-Modified Glass Ionomer Cement in Comparison to Conventional Polyacrylic Acid.
Photobiomodul Photomed Laser Surg
January 2025
Department of Preventive Dental Sciences, College of Dentistry, Dar Al Uloom University, Riyadh, Saudi Arabia.
Impact of surface conditioner phytic acid (IP6) Er,Cr:YSGG laser (ECYL) methylene blue photodynamic therapy (MB-PDT) on the microleakage and shear bond strength (SBS) of resin-modified glass ionomer cement (RMGIC) to primary sound dentin. Overall, 80 extracted sound primary molars were collected followed by their submergence in self-cure acrylic resin. The dentin surface was exposed and made flat and was assigned into four groups based on the surface conditioning.
View Article and Find Full Text PDFBonding performance of universal adhesive systems with dual-polymerising resin cements to various dental substrates: in vitro study.
BMC Oral Health
January 2025
Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Institute of Science Tokyo, 1-5-45 Yushima, Bunkyo-Ku, Tokyo, 113-8549, Japan.
Background: Resin cements often require substrate-specific pretreatment. Recently, universal adhesive systems have been introduced, simplifying procedures by eliminating the need for multiple adhesives and offering options that do not require light curing. This study investigated the bonding performance of universal adhesive systems combined with dual-polymerising resin cements on enamel, dentin, zirconia, lithium disilicate ceramics (LDS), and resin blocks.
View Article and Find Full Text PDFMethacrylic acid/Tween 80 engineered amorphous calcium phosphate as an effective bioactive reinforcing nanofillers in dental adhesive.
Dent Mater J
January 2025
Department of Chemistry, Faculty of Science, Kasetsart University.
Bioactive fillers in dental adhesives are designed to release beneficial ions, such as calcium and phosphate, to help in remineralization process, and preventing secondary caries. Their incorporation also aims to improve the longevity of dental restorations. Herein, CaP nanoparticles were synthesized through a water-in-oil emulsion method using Tween80 as a surfactant and methacrylic acid (MAA).
View Article and Find Full Text PDFInfluence of surface treatments on highly translucent zirconia: Mechanical, optical properties and bonding performance.
J Dent
January 2025
State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, Key Laboratory of Oral Biomedicine Ministry of Education, Hubei Key Laboratory of Stomatology, School & Hospital of Stomatology, Wuhan University, Wuhan 430079, China. Electronic address:
Objectives: Highly translucent yttria-stabilized zirconia (YSZ) has become more popular due to its enhanced aesthetics. This study aimed to evaluate the influence of traditional air abrasion and a new etching and cleaning agent, Multi Etchant, on the mechanical performance, optical properties, and bond strength of highly translucent zirconia.
Methods: Specimens of 6YSZ, 5YSZ, 4YSZ&5YSZ, and conventional 3YSZ were fabricated and underwent different surface treatments, including as milled, air abrasion, and Multi Etchant.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!