Objective. This study evaluated the effect of immediate or delayed finishing/polishing using different systems on the surface roughness, hardness, and microleakage of a silorane-based composite. Material and Methods. Specimens were made with silorane-based composite (Filtek P90, 3M ESPE) and assigned to the treatments: control (light-cured); aluminum oxide discs (Sof-Lex, 3M ESPE); diamond-impregnated silicone tips (Astropol, Ivoclar Vivadent); aluminum oxide-impregnated silicone tips (Enhance, Dentsply). Half of the specimens were finished/polished immediately and the rest after 7 days. Surface roughness (Ra, μm; n = 20) and Vickers microhardness (50 g; 45 s; n = 10) were measured. Cavities were prepared in bovine incisors and filled with Filtek P90. The fillings received immediate or delayed finishing/polishing (n = 10) and were subjected to dye penetration test (0.5% basic fuchsin, 24 h). Data were analyzed by ANOVA and Scheffe, Kruskal-Wallis, and Mann-Whitney tests (p < 0.05). Results. The finishing/polishing system significantly influenced roughness and microhardness (p < 0.0001). For enamel, microleakage was not affected by the finishing/polishing system (p = 0.309). For dentin, Sof-Lex discs and Astropol points promoted greater microleakage than Enhance points (p = 0.033). Conclusion. Considering roughness, microhardness, and microleakage together, immediate finishing/polishing of a silorane-based composite using aluminum oxide discs may be recommended.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4762996 | PMC |
| http://dx.doi.org/10.1155/2016/8346782 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Pre-Heating of Low-Shrinkage Composite Resins: Effects on Color Stability and Surface Roughness.
Front Dent
August 2022
Department of Orthodontics, Faculty of Dentistry, Tabriz Azad University of Medical Sciences, Tabriz, Iran.
The present study aimed to investigate the effect of preheating on the color stability and surface roughness of a silorane-based composite resin. A total of 44 Filtek P90 composite resin disks, (10mm×1mm), were fabricated using plastic molds and were divided into two groups. In group 2, the composite resin syringes were placed in a thermostatically controlled water bath at 55‒60°C before preparing the disks.
View Article and Find Full Text PDFThe Effect of Thermocycling on Interfacial Bonding Stability of Self-Etch Adhesives: OCT Study.
Biomed Res Int
September 2021
Department of Restorative Dentistry, Faculty of Dentistry, King Abdulaziz University, P.O. Box 80209, Jeddah 215-89, Saudi Arabia.
Objective: The aim of this study was to monitor the behavior of interfacial gaps formed under different bonded polymeric restorations before and after thermocycling (TC), using swept-source optical coherence tomography (SS-OCT) and confirming the obtained findings with confocal laser scanning microscopy (CLSM).
Materials And Methods: Cylindrical class I cavities were prepared in twenty noncarious human premolar teeth (1.5 mm depth × 3.
Elution of rifampin and vancomycin from a weight-bearing silorane-based bone cement.
Bone Joint Res
April 2021
Department of Orthopaedic Surgery, University of Kansas Medical Center, Kansas City, Kansas, USA.
Aims: Poly(methyl methacrylate) (PMMA)-based bone cements are the industry standard in orthopaedics. PMMA cement has inherent disadvantages, which has led to the development and evaluation of a novel silorane-based biomaterial (SBB) for use as an orthopaedic cement. In this study we test both elution and mechanical properties of both PMMA and SBB, with and without antibiotic loading.
View Article and Find Full Text PDFMinimal intervention in dentistry: which is the best approach for silorane composite restoration repairs?
J Clin Exp Dent
April 2021
DDS, Ms, PhD. Department of Restorative Dentistry, Institute of Science and Technology, São Paulo State University-UNESP, São Paulo, Brazil.
Background: This study aimed to evaluate surface treatments, adhesives and composites for repairing silorane based restorations.
Material And Methods: One hundred and twenty truncated cones (2 mm smaller diameter and 4 mm larger diameter) made of silorane composite were divided in 12 groups according with the surface treatment (diamond bur and oxide aluminum abrasion), the adhesive (Adper Scothbond Multipurpose (3M ESPE), Ecusit (Voco) and Filtek P90 Adhesive (3M ESPE)). Each group was subdivided in two according with the composite used for repair (methacrylate and silorane).
Analysis of microleakage and marginal gap presented by new polymeric systems in class V restorations: An study.
Saudi Dent J
March 2021
Department of Health Sciences, University of Southern Santa Catarina, Tubarão, Brazil.
Objective: Evaluating the contraction of polymerization effect of silorane-based composite on dental interface in enamel.
Materials And Methods: Eighty class V cavities were confectioned in forty extracted molar teeth and restored with different combinations of resinous-based and bond system. They were divided into the following groups: (G1) three-step etch-and-rinse adhesive system and methacrylate-based resin, (G2) two-step etch-and-rinse adhesive system and methacrylate-based resin, (G3) Filtek P-90 self-conditioning adhesive system and methacrylate-based resin, (G4) Adper SE Plus self-conditioning adhesive system and methacrylate-based resin, (G5) three-step etch-and-rinse adhesive system and silorane-based resin, (G6) two-step etch-and-rinse adhesive system and silorane-based resin, (G7) Filtek P-90 self-conditioning adhesive system and silorane-based resin, (G8) Adper SE Plus self-conditioning adhesive system and silorane-based resin.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!