Effect of Tooth-structure Thickness on Light Attenuation and Depth of Cure.

Newer bulk-fill composites claim a greater depth of cure than conventional resin-based composites. To facilitate complete curing, the manufacturer of SonicFill (Kerr) recommends curing from the occlusal, as well as the buccal and lingual, surfaces of the tooth. The purpose of this study was to quantify the degree of curing light attenuation as it passes through natural tooth structure, and how this attenuation affects the depth of cure of different posterior resin composites. Ten noncarious extracted mandibular third molars were sectioned to produce 5-mm-thick pieces of buccal tooth structure. Sanding 0.5-mm increments from the flattened surface produced 4.5-, 4.0-, 3.5-, 3.0-, 2.5-, 2.0-, and finally 1.5-mm-thick sections. A Bluephase G2 (Ivoclar) curing light with an 8-mm-diameter light guide set on high for 20 seconds was used for measurement of irradiance as it passed through different thicknesses of tooth structure and air. The average irradiance (mW/cm(2)) was measured with a MARC-RC Resin Calibrator with a 4-mm-diameter sensor (BlueLight Analytics). To measure depth of cure of a conventional hybrid composite (Herculite Ultra; Kerr) vs a bulk-fill hybrid composite (SonicFill) through varying thicknesses of tooth structure, composites were cured in a 4-mm-diameter × 10.25-mm-long split mold according to International Organization for Standardization 4049. A mean and standard deviation was determined per group. Data were analyzed with a one-way analysis of variance (ANOVA)/Tukey test and two-way ANOVA/Tukey test (α=0.05). One-way ANOVA/Tukey found a significant decrease in irradiance based on thickness of tooth structure or distance through air (p<0.001). Two-way ANOVA/Tukey found a significant decrease in depth of cure based on thickness of tooth structure (p<0.001) and on composite type (p<0.001) with no significant interaction (p=0.623). SonicFill had a significantly greater depth of cure than Herculite Ultra.