Are self-adhesive resin cements suitable as core build-up materials? Analyses of maximum load capability, margin integrity, and physical properties.

Objectives: The aim of the present study was to test a self-adhesive resin cement used as core build-up material in comparison to two commercially available core build-up materials.

Materials And Methods: Forty human anterior teeth were endodontically treated and fiber post insertion (RelyX Fiber posts) and core build-ups were performed using two core build-up materials applied with an etch-and-rinse adhesive approach (Luxacore Dual-LC and Clearfil Core-CC) and an experimental self-adhesive resin cement (SAR) in two application modes (SAR Handmix and SAR Automix). Samples were subjected to thermo-mechanical loading. Margin integrity was determined using scanning electron microscopy (SEM), and maximum load capability (Fmax) was evaluated. Physical properties of the tested materials were also examined.

Results: Fmax was significantly affected by the core build-up material (p < 0.0005; one-way ANOVA). CC [481 (158) N] revealed significantly higher Fmax compared to LC [226 (80) N], SAR Hand [205 (115), and SAR Automix [197 (134) N] (p < 0.05; Tukey-B). The percentage of margin quality "continuous margin" in enamel after thermo-mechanical loading (TML) differed significantly among groups (p < 0.0005; Kruskal-Wallis); CC demonstrated a significantly higher percentage of margin quality "continuous margin" compared to the other groups. Physical properties were significantly affected by the different core materials (p < 0.0005; ANOVA); CC and LC demonstrated significantly higher flexural strength compared to both SAR groups as well as significantly higher water sorption of both SAR groups compared to CC and LC.

Conclusion: Within the limitations of the present in vitro study, we conclude that the investigated experimental self-adhesive resin cement is not suitable as a core build-up material due to the lower maximum load capability, low margin quality, and the data of the mechanical properties.

Clinical Relevance: The investigated experimental self-adhesive resin cement cannot be recommended as a core build-up material.