The effect of polymerization cycles on flexural properties of conventional (Vipi Cril(®)-VC) or microwave-processed (Vipi Wave(®)-VW) denture base acrylic resins was evaluated. Specimens (n=10) were submitted to the cycles: WB=65ºC for 1 h+1 h boiling water (VC cycle); M630/25=10 min at 270 W+5 min at 0 W+10 min at 360 W (VW cycle); M650/5=5 min at 650 W; M700/4=4 min at 700 W; and M550/3=3 min at 550 W. Specimens were submitted to a three-point bending test at 5 mm/min until fracture. Flexural strength (MPa) and elastic modulus (GPa) data were analyzed by 2-way ANOVA/Tukey HSD (α=0.05). Overall, VC showed higher values than VW. The results obtained with microwave polymerization did not differ from those obtained with water-bath for both acrylic resins. The results observed when polymerization cycles using medium power and shorter time were used did not differ from those when manufacturer's recommended microwave cycle was applied. Conventional VC might be microwave-processed without compromising its flexural properties.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4012/dmj.2015-047 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Silver nanoparticles immobilized on crosslinked vinyl polymer for catalytic reduction of nitrophenol: experimental and computational studies.
Sci Rep
January 2025
Chemistry Department, Faculty of Science, Damietta University, New Damietta, 34517, Egypt.
The removal of toxic nitrophenols from the industrial wastewater is urgently needed from health, environmental and economic aspects. The present study deals with the synthesis of crosslinked vinyl polymer Poly(divinylbenzene) (poly(DVB)) through free radical polymerization technique using AIBN as initiator and acetonitrile as solvent. The prepared polymer was used as a support for silver nanoparticles via chemical reduction of silver nitrate on the polymer network.
View Article and Find Full Text PDFHigh-Rate 4.2 V Solid-State Potassium Batteries by In Situ Polymerized Epoxide Ether Electrolyte.
Nano Lett
January 2025
College of Materials Science and Engineering, Hunan Joint International Laboratory of Advanced Materials and Technology of Clean Energy, Hunan Province Key Laboratory for Advanced Carbon Materials and Applied Technology, Hunan University, Changsha 410082, China.
Solid-state metallic potassium batteries (SSMPBs) afresh have attracted incremental attention because of their potential to supplement solid-state metallic lithium batteries. However, SSMPBs suffer poor electrochemical performances due to the low ionic conductivity of solid electrolytes and huge electrode/electrolyte interfacial resistance. Herein, high-rate SSMPBs are achieved by in situ ring-opening polymerization of 1,3-dioxolane with succinonitrile as a plasticizer and Al(OTf) as the catalyst, where the succinonitrile enables short-chain polyether electrolytes.
View Article and Find Full Text PDFSulfonated White-Graphene for High-Performance Gel Polymer Electrolytes: The Interplay between Ion Conductivity and Rheology.
Small
January 2025
Department of Chemical Engineering, Toronto Metropolitan University, 350 Victoria Street, Toronto, ON, M5B 2K3, Canada.
Research into flexible solid-state supercapacitors for wearable electronics focuses on achieving high performance and safety. Gel polymer electrolytes (GPEs) are preferred over fully solid-state electrolytes due to their better ionic conductivity while addressing safety concerns associated with liquid electrolytes. This study aims to enhance high-performance gel polymer electrolytes (HP-GPEs) by improving the ion transfer rate of polyvinyl alcohol (PVA) with sulfonated hexagonal boron nitride (known as white-graphene) and exploring how rheology influences ion-conduction within HP-GPEs.
View Article and Find Full Text PDFAn Oriented Interpenetrating Network Structure Multi-Stimuli Responsive Hydrogel.
Macromol Rapid Commun
January 2025
Key Laboratory of Multi-Scale Manufacturing Technology, Chongqing Institute of Green and Intelligent Technology, Chinese Academy of Sciences, Chongqing College, University of Chinese Academy of Sciences, Chongqing, 400714, P. R. China.
As a recent focal point of research, soft electronics encompass various factors that synergistically enhance their mechanical properties and ensure stable electrical performance. However, challenges such as immiscible conductive fillers, poor phase interfaces, and unstable conductive networks hinder the overall efficacy of these materials. To address these issues, a hydrogel featuring an oriented interpenetrating network structure (OIPN) is developed.
View Article and Find Full Text PDFOvarian steroids modulate mRNA expression of ECM associated genes and collagen deposition induced by TGF β1 in equine endometrium in vitro.
Sci Rep
January 2025
Institute of Animal Reproduction and Food Research, Polish Academy of Sciences, Olsztyn, 10-748, Poland.
Equine endometrosis is a major cause of infertility in mares and is characterized by degenerative, functional and fibrotic changes in the endometrium with increased collagen (COL) deposition. Transforming growth factor (TGF)-β1 is one of the major pro-fibrotic factors involved in the excessive deposition of extracellular matrix (ECM) components in the equine endometrium. It has been demonstrated that ovarian steroids, specifically 17β-estradiol (E2) and progesterone (P4), not only regulate the cyclicity of the estrous cycle, but also have been implicated as anti- or pro-fibrotic factors.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!