Synthesis and Photoluminescent Properties of Nanorod Bundle Ln4O(OH)9NO3:Eu(Ln = Y, Lu) Prepared by Hydrothermal Method.

Well-crystallized nanorod bundles Ln4O(OH)9NO3:1%Eu(Ln = Y, Lu) have been successfully prepared by hydrothermal method. The crystalline phase, size and optical properties were characterized using powder X-ray diffraction (XRD), field emission-scanning electron microscopy (FE-SEM), infrared (IR) spectrograph and photoluminescent (PL) spectra. Site occupations of Eu3+ in crystals Ln4O(OH)9NO3:Eu(Ln = Y, Lu) were discussed based on excitation spectra and the empirical relationship formula between the charge transfer (CT) energy and the environmental factor. The emission spectra exhibited that the strongest emission peaks with an excitation wavelength of 395 nm were at 617 and 626 nm in crystal Lu4O(OH)9NO3:1%Eu and Y4O(OH)9NO3:1%Eu, respectively, both of which come from 5D0-7F2 transition of the Eu3+ ions. The broad excitation peaks at about 254 and 255 nm were found when monitored at 617 and 628 nm in crystal Lu4O(OH)9NO3:1%Eu and Y4O(OH)9NO3:1%Eu, respectively, which were due to O-Eu CT transition. Based on the dielectric theory of complex crystal, the CT bands at about 254 and 255 nm in Ln4O(OH)9NO3:1%Eu(Ln = Y, Lu) were assigned to the transition of O-Eu at Ln3(Ln = Y, Lu) site, from which we can conclude that Eu3+ ions occupied the site of Ln3(Ln = Y, Lu) in crystal Ln4O(OH)9NO3:1%Eu(Ln = Y, Lu). It put forward a new route to investigate site occupation of luminescent center ions in rare earth doped complex inorganic luminescence materials.