Resin-based composites show similar kinetic profiles for dimensional change and recovery with solvent storage.

Objectives: To investigate the sorption, solubility, mass change and hygroscopic expansion (solvent swelling) of resin-composites after long term storage in different solvents.

Methods: Eight materials were studied: two bulk-fill flowable materials (SDR and Venus bulk fill, V-BF), a packable bulk-fill material (Tetric Evoceram bulk-fill, TET-BF), a fiber reinforced material (Ever X posterior, EVX), a nano-hybrid conventional material (Tetric Evoceram, TET) and micro-hybrid conventional materials (G-aenial anterior, GA-P and posterior, GA-A). Three groups of disk shaped specimens were prepared using split stainless steel molds. Each group was stored, respectively, in: water, 75% ethanol/water and methyl ethyl ketone (MEK). The total storage time was 180 d plus a reconditioning time of 120 d. A non-contact laser scanning micrometer was used to measure the diametral changes.

Results: Significant differences were found in the sorption and solubility of the materials. Generally, MEK stored specimens had the highest values followed by 75% ethanol/water then water. A similar trend was found with the mass and volume changes (except for EVX). V-BF showed the highest sorption (98.1μg/mm(3)) and solubility (10μg/mm(3)) after MEK storage. Mass and volume changes showed near-linear correlation, with high Pearson coefficients (0.86-0.99).

Significance: Generally the materials were most greatly affected by MEK storage compared to the other two solvents. The glass-fiber-reinforced EVX, however, was most affected by water immersion. The pattern of change/recovery behavior of the materials, during solvent challenge, was similar to the pattern of viscoelastic creep/recovery behavior of resin-composite materials.