Ultrafast Spectroscopy and Red Emission from β-Ga2O 3/β-Ga 2S 3 Nanowires.

Ultrafast pump-probe and transient photoluminescence spectroscopy were used to investigate carrier dynamics in β-Ga2O3 nanowires converted to β-Ga2O3/Ga2S3 under H2S between 400 to 600 °C. The β-Ga2O3 nanowires exhibited broad blue emission with a lifetime of 2.4 ns which was strongly suppressed after processing at 500-600 °C giving rise to red emission centered at 680 nm with a lifetime of 19 μs. Differential absorption spectroscopy reveals that state filling occurs in states located below the conduction band edge before sulfurization, but free carrier absorption is dominant in the β-Ga2O3/Ga2S3 nanowires processed at 500 to 600 °C for probing wavelengths >500 nm related to secondary excitation of the photo-generated carriers from the mid-gap states into the conduction band of Ga2S3.