Changes to the Disordered Phase and Apatite Crystallite Morphology during Mineralization by an Acidic Mineral Binding Peptide from Osteonectin.

Noncollagenous proteins regulate the formation of the mineral constituent in hard tissue. The mineral formed contains apatite crystals coated by a functional disordered calcium phosphate phase. Although the crystalline phase of bone mineral was extensively investigated, little is known about the disordered layer's composition and structure, and less is known regarding the function of noncollagenous proteins in the context of this layer. In the current study, apatite was prepared with an acidic peptide (ON29) derived from the bone/dentin protein osteonectin. The mineral formed comprises needle-shaped hydroxyapatite crystals like in dentin and a stable disordered phase coating the apatitic crystals as shown using X-ray diffraction, transmission electron microscopy, and solid-state NMR techniques. The peptide, embedded between the mineral particles, reduces the overall phosphate content in the mineral formed as inferred from inductively coupled plasma and elemental analysis results. Magnetization transfers between disordered phase species and apatitic phase species are observed for the first time using 2D (1)H-(31)P heteronuclear correlation NMR measurements. The dynamics of phosphate magnetization transfers reveal that ON29 decreases significantly the amount of water molecules in the disordered phase and increases slightly their content at the ordered-disordered interface. The peptide decreases hydroxyl to disordered phosphate transfers within the surface layer but does not influence transfer within the bulk crystalline mineral. Overall, these results indicate that control of crystallite morphology and properties of the inorganic component in hard tissue by biomolecules is more involved than just direct interaction between protein functional groups and mineral crystal faces. Subtler mechanisms such as modulation of the disordered phase composition and structural changes at the ordered-disordered interface may be involved.