On self-assembled monolayer-covered Cu-Au substrates, localized volume shrinkage at initial dealloying sites leads to cracks within the attacked regions. It is started from well-controlled surface structures to gain fundamental insights in the driving mechanisms of localized corrosion and crack formation. Both the crack density and the crack morphology are critically dependent on surface orientation, crystallography, and inhibitor molecule species.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1002/adma.201405565 | DOI Listing |
Publication Analysis
Top Keywords
star-shaped crystallographic
4
crystallographic cracking
4
cracking localized
4
localized nanoporous
4
nanoporous defects
4
defects self-assembled
4
self-assembled monolayer-covered
4
monolayer-covered cu-au
4
cu-au substrates
4
substrates localized
4
Similar Publications
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!