Unlabelled: Fatigue of resin-dentin adhesive bonds is critical to the longevity of resin composite restorations.
Objectives: The objectives were to characterize the fatigue and fatigue crack growth resistance of resin-dentin bonds achieved using two different commercial adhesives and to identify apparent "weak-links".
Methods: Bonded interface specimens were prepared using Adper Single Bond Plus (SB) or Adper Scotchbond Multi-Purpose (SBMP) adhesives and 3M Z100 resin composite according to the manufacturers' instructions. The stress-life fatigue behavior was evaluated using the twin bonded interface approach and the fatigue crack growth resistance was examined using bonded interface Compact Tension (CT) specimens. Fatigue properties of the interfaces were compared to those of the resin-adhesive, resin composite and coronal dentin.
Results: The fatigue strength of the SBMP interface was significantly greater than that achieved by SB (p≤0.01). Both bonded interfaces exhibited significantly lower fatigue strength than that of the Z100 and dentin. Regarding the fatigue crack growth resistance, the stress intensity threshold (ΔKth) of the SB interface was significantly greater (p≤0.01) than that of the SBMP, whereas the ΔKth of the interfaces was more than twice that of the parent adhesives.
Significance: Collagen fibril reinforcement of the resin adhesive is essential to the fatigue crack growth resistance of resin-dentin bonds. Resin tags that are not well hybridized into the surrounding intertubular dentin and/or poor collagen integrity are detrimental to the bonded interface durability.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4792123 | PMC |
| http://dx.doi.org/10.1016/j.dental.2015.06.011 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Fatigue Experiment and Failure Mechanism Analysis of Aircraft Titanium Alloy Wing-Body Connection Joint.
Sensors (Basel)
December 2024
Department of Industrial Engineering and Management, Shanghai Jiao Tong University, Shanghai 200240, China.
Taking the titanium alloy wing-body connection joint at the rear beam of a certain type of aircraft as the research object, this study analyzed the failure mechanism and verified the structural safety of the wing-body connection joint under actual flight loads. Firstly, this study verified the validity of the loading system and the measuring system in the test system through the pre-test, and the repeatability of the test was analyzed for error to ensure the accuracy of the experimental data. Then, the test piece was subjected to 400,000 random load tests of flight takeoffs and landings, 100,000 Class A load tests, and ground-air-ground load tests, and the test piece fractured under the ground-air-ground load tests.
View Article and Find Full Text PDFA Time Series Proposal Model to Define the Speed of Carbon Steel Corrosion in an Extreme Acid Environment.
Materials (Basel)
December 2024
Sustainable Mining Engineering Research Group, Department of Mining, Mechanic, Energetic and Construction Engineering, Higher Technical School of Engineering, University of Huelva, 21007 Huelva, Spain.
This article shows the behavior of the corrosive effect of acid mine water on carbon steel metal alloys. Mining equipment, composed of various steel alloys, is particularly prone to damage from highly acidic water. This corrosion results in material thinning, brittle fractures, fatigue cracks, and ultimately, equipment failure.
View Article and Find Full Text PDFDifferences in Rejuvenation Mechanisms and Physical Properties of Aged Styrene-Butadiene-Styrene (SBS)-Modified Bitumen by Mono-Epoxy and Di-Epoxy Compounds.
Polymers (Basel)
December 2024
Key Laboratory for Special Area Highway Engineering of Ministry of Education, Chang'an University, South 2nd Ring Road Middle Section, Xi'an 710064, China.
Studying the mechanisms and effects of rejuvenators on SBS-modified bitumen is crucial for repairing degraded SBS and recycling aged SBS-modified bitumen (ASMB), thereby contributing to the sustainable development of bitumen pavements. This research examines the roles of mono-epoxy Alkyl (C12-C14) glycidyl ether (AGE) and di-epoxy 1,6-Hexanediol diglycidyl ether (HDE) under the catalysis of N,N-dimethyl benzyl amine (BDMA) in repairing degraded SBS chains. Aromatic oil (ORSMB)-, AGE-aromatic oil (ARSMB)-, and HDE-aromatic oil (HRSMB)-rejuvenated bitumen are analyzed for their chemical structures, physical properties, and rheological properties.
View Article and Find Full Text PDFModeling hydrogen-assisted fatigue crack growth in low-carbon steel focusing on thermally activated hydrogen-dislocation interaction.
Sci Technol Adv Mater
December 2024
Research Center for Structural Materials, National Institute for Materials Science (NIMS), Tsukuba, Japan.
Hydrogen-assisted (HA) fatigue crack growth (FCG) occurs in ferritic steels, wherein H-dislocation interaction plays a vital role. We aim to model the HAFCG mechanism based on the within the crack tip zone. Our modeling framework is as follows: H is condensed into crack tip and trapped by dislocations; these H significantly decrease dislocation mobility; stress relief via crack blunting is suppressed; localized brittle fracture triggers HAFCG.
View Article and Find Full Text PDFInfluence of Operating Temperature on Crack Growth Characteristics and Fatigue Life Prediction of Carbon Black-Filled Hydrogenated Nitrile Butadiene Rubber.
Polymers (Basel)
December 2024
College of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, China.
Rubber is widely used in situations involving cyclic loads, and the influence of temperature on rubber properties is particularly pronounced under cyclic loading. In this study, mechanical property tests and crack propagation tests of carbon black-filled hydrogenated nitrile butadiene rubber were conducted at four different operating temperatures. Based on the results of the crack propagation tests, the temperature-dependent characteristics of the Paris-Erdogan parameters and strain energy density were clarified.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!